Abstract:The purpose of this study is to investigate the mechanism of improving fatigue performance and the estimation model of fatigue life for corroded steel plate strengthened with CFRP plates. A new two-stage fatigue crack propagation prediction model for the corroded steel plate strengthened with CFRP plates was proposed; moreover, the identification of critical rust pits and the equivalent method of initial cracks, and the calculation method of stress intensity factor (SIF) values at the crack tip were established. The accuracy of the proposed model was verified by comparing the predicted and tested fatigue life of the corroded steel plate strengthened with CFRP plates. Finally, the proposed two-stage crack propagation model was applied to carry out a parameter analysis to investigate the effect of weight loss rate, equivalent initial crack size, adhesive thickness, CFRP stiffness and CFRP prestress level on the fatigue crack propagation of the corroded steel plate strengthened with CFRP plates. Results showed that the maximum depth and the average width of the rust pits were suggested to be taken as the equivalent dimensions of the initial semi-elliptical surface crack for the fatigue crack propagation prediction of corroded steel plate strengthened with CFRP plates. Increasing the weight loss rate of the corroded steel plate, the initial crack size or the adhesive thickness would accelerate the crack growth and reduce the fatigue life, whereas increasing the stiffness or prestress level of the CFRP plate would significantly reduce the crack growth rate and increase the fatigue life. The smaller the initial crack size, the more sensitive the crack propagation life was to the variation of equivalent initial crack size. The influence of adhesive thickness on the fatigue life was limited and convergent, and the application of prestressing could significantly improve the utilization rate of CFRP materials and the fatigue strengthening effect of the corroded steel plate.

Experimental study on mixed-mode fatigue behavior of center cracked steel plates repaired with CFRP materials

Fatigue behavior and digital image correlation monitoring of steel plates with mixed-mode edge cracks repaired with CFRP materials

Experimental study on dynamic behavior of CFRP-to-steel interface

Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

STUDY ON FATIGUE BEHAVIOR OF CRACKED TENSILE STEEL PLATES REINFORCED WITH CFRP PLATES

Fatigue Behavior of Cracked High-Strength Steel Plates Strengthened by CFRP Sheets

Cracking Behavior of Cfrp Laminate-Strengthened Rc Beams with Premechanical and Postmechanical Environmental Damage

Experimental Study on Fatigue Behavior of Tensile Steel Plates Strengthened with CFRP Plates

Repairing Behaviors of Cracked Steel Plates Based on Bolted Fiber-Reinforced Polymer Plates

Debonding development in cracked steel plates strengthened by CFRP laminates under fatigue loading: Experimental and boundary element method analysis

Study on thermal effects on fatigue behavior of cracked steel plates strengthened by CFRP sheets

Prediction of Bending Fatigue Life of Cracked Out-of-Plane Gusset Joint Repaired by CFRP Plates

Fatigue performance of carbon fiber‐reinforced polymer strengthened single‐edge cracked steel plates: Effects of adhesive property and CFRP arrangement

Crack Propagation and Debonding Development of CFRP Laminate Strengthened High-Strength Steel Plates under Fatigue Loadings

The Effect of Patch Geometry on the Static and Fatigue Behaviors of Defective Aluminum Panels Repaired with A Composite Patch

Experimental Study on Interfacial Bond Behavior between CFRP Sheets and Steel Plates under Fatigue Loading

Fatigue Crack Propagation Prediction of Corroded Steel Plate Strengthened with Carbon Fiber Reinforced Polymer (CFRP) Plates

Fatigue Life Appraisal and Its Corrected Stress Intensity Factor for Repaired Off-CentrallyCracked Aluminum Plates

Finite Element Analysis for the Fatigue Behavior of Steel Plates Strengthened with CFRP Plates

Study on flexural performance of cracked RC beams retrofitted with CFRP sheets

PARAMETER STUDY ON STEEL PLATES REINFORCED BY CFRP PLATES WITH FINITE ELEMENT METHOD