Abstract:Here, a hydrometallurgical process was proposed to separate nickel (Ni) and iron (Fe) from ferronickel. The effects of different factors, namely hydrothermal temperature, initial Fe 2+ concentration, and Ni 2+ concentration, on the hematite precipitation process, were detail investigated. Ferronickel powders were leached using a 120 g/L H 2 SO 4 solution at 85 °C for 8 h. The final pH of the leaching solution was controlled at 3.0−4.5, and the Fe 2+ concentration was maintained at 50−60 g/L. Copper from the ferronickel powder was first leached in the early stage of the leaching process, and then it was reduced by an excess of ferronickel powder, leading to its enrichment in the leaching residue. Approximately 50 g/L of Fe ions was successfully removed and precipitated as hematite containing 60% Fe, 0.3% Ni, and 1.5% S during hydrothermal precipitation at 200 °C for 3 h. Through evaporation crystallization at 90 °C for 8 h, large particles of nickel sulfate hexahydrate (NiSO 4 ·6H 2 O) containing 19.4% Ni, 0.074% Fe, and 10.69% S were obtained. Moreover, through freezing crystallization at −8 °C for 1 h, smaller particles of NiSO 4 ·6H 2 O product containing 20.3% Ni, 0.014% Fe, and 11.13% S were synthesised. Ici, on a proposé un procédé hydrométallurgique basé sur la lixiviation atmosphérique à l'acide sulfurique et précipitation d'hématite pour la séparation du nickel (Ni) et du fer (Fe) à partir du ferronickel. On a étudié en détail les effets de différents facteurs, dont la température hydrothermale, la concentration initiale de Fe 2+ et la concentration de Ni 2+ sur le procédé de précipitation de l'hématite. On a traité par lixiviation les poudres de ferronickel en utilisant 120 g/L d'une solution de H 2 SO 4 à 85°C pendant 8 h. On a contrôlé le pH final de la solution de lixiviation entre 3.0 et 4.5 et la concentration de Fe 2+ a été maintenue entre 50 et 60 g/L. Le cuivre de la poudre de ferronickel était d'abord traité par lixiviation au début du procédé de lixiviation, puis il a été réduit par un excès de poudre de ferronickel, conduisant à son enrichissement dans le résidu de lixiviation. Environ 50 g/L d'ions Fe ont été éliminés avec succès et précipités sous forme d'hématite contenant 60% de Fe, 0.3% de Ni et 1.5% de S lors d'une précipitation hydrothermale à 200°C pendant 3 h. Grâce à une cristallisation par évaporation à 90°C pendant 8 h, on a obtenu de grosses particules de sulfate de nickel hexahydraté (NiSO 4 ·6H 2 O) contenant 19.4% de Ni, 0.074% de Fe et 10.69% de S. De plus, on a synthétisé, grâce à la cristallisation par congélation à – 8°C pendant 1 h, des particules plus petites du produit NiSO 4 ·6H 2 O contenant 20.3% de Ni, 0.014% de Fe et 11.13% de S.

Utilization of Limonitic Nickel Laterite to Produce Ferronickel Concentrate by the Selective Reduction-Magnetic Separation Process

Efficient Utilization of Limonite Nickel Laterite to Prepare Ferronickel by the Selective Reduction Smelting Process

Extraction of ferronickel concentrate from laterite nickel ore by reduction roasting-magnetic separation using spent cathode carbon

Preparing Ferro-Nickel Alloy from Low-Grade Laterite Nickel Ore Based on Metallized Reduction–Magnetic Separation

Separation and Recovery of Iron and Nickel from Low-Grade Laterite Nickel Ore by Microwave Carbothermic Reduction Roasting

Mechanism of Calcium Sulphate on the Aggregation and Growth of Ferronickel Particles in the self-Reduction of Saprolitic Nickel Laterite Ore

Valorization of Solid Residue from the Lateritic Nickel Ore Leaching Process for Ferronickel Production

Recovery of nickel and iron from ferronickel powder and high nickel matte via the atmospheric leaching-hematite precipitation process

Extraction of Nickel from Garnierite Laterite Ore Using Roasting and Magnetic Separation with Calcium Chloride and Iron Concentrate

Reduction of limonite ore from South Sulawesi with additive Na2SO4 using carbon monoxide

A Novel Utilization of Bayer Red Mud Through Co-Reduction with a Limonitic Laterite Ore to Prepare Ferronickel

Reductive behavior of nickel and iron metallization in magnesian siliceous nickel laterite ores under the action of sulfur-bearing natural gas

The Separation and Enrichment of Nickel from Leachate of Nickeliferous Laterite by Using Sulfate Crystallization

Mineralogical Characterization of Limonitic Laterite from Africa and Its Proposed Processing Route

The High Temperature Co-Processing of Nickel Sulfide and Nickel Laterite Sources

Effect of CaF2 on the Aggregation and Growth of Ferronickel Particles in the Self-Reduction of Nickel Laterite Ore

Analysis of holding time variations to Ni and Fe content and morphology in nickel laterite limonitic reduction process by using coal-dolomite bed

Separation of nickel and iron from ferronickel via sulfuric acid leaching and hydrothermal precipitation

Mineralogical Characterisation of a Sample of an Australian Nickel Laterite

Characterization of fluidized reduction roasting of nickel laterite ore under CO/CO2 atmosphere

A Robust Recovery of Ni From Laterite Ore Promoted by Sodium Thiosulfate Through Hydrogen-Thermal Reduction