Abstract:Here, a hydrometallurgical process was proposed to separate nickel (Ni) and iron (Fe) from ferronickel. The effects of different factors, namely hydrothermal temperature, initial Fe 2+ concentration, and Ni 2+ concentration, on the hematite precipitation process, were detail investigated. Ferronickel powders were leached using a 120 g/L H 2 SO 4 solution at 85 °C for 8 h. The final pH of the leaching solution was controlled at 3.0−4.5, and the Fe 2+ concentration was maintained at 50−60 g/L. Copper from the ferronickel powder was first leached in the early stage of the leaching process, and then it was reduced by an excess of ferronickel powder, leading to its enrichment in the leaching residue. Approximately 50 g/L of Fe ions was successfully removed and precipitated as hematite containing 60% Fe, 0.3% Ni, and 1.5% S during hydrothermal precipitation at 200 °C for 3 h. Through evaporation crystallization at 90 °C for 8 h, large particles of nickel sulfate hexahydrate (NiSO 4 ·6H 2 O) containing 19.4% Ni, 0.074% Fe, and 10.69% S were obtained. Moreover, through freezing crystallization at −8 °C for 1 h, smaller particles of NiSO 4 ·6H 2 O product containing 20.3% Ni, 0.014% Fe, and 11.13% S were synthesised. Ici, on a proposé un procédé hydrométallurgique basé sur la lixiviation atmosphérique à l'acide sulfurique et précipitation d'hématite pour la séparation du nickel (Ni) et du fer (Fe) à partir du ferronickel. On a étudié en détail les effets de différents facteurs, dont la température hydrothermale, la concentration initiale de Fe 2+ et la concentration de Ni 2+ sur le procédé de précipitation de l'hématite. On a traité par lixiviation les poudres de ferronickel en utilisant 120 g/L d'une solution de H 2 SO 4 à 85°C pendant 8 h. On a contrôlé le pH final de la solution de lixiviation entre 3.0 et 4.5 et la concentration de Fe 2+ a été maintenue entre 50 et 60 g/L. Le cuivre de la poudre de ferronickel était d'abord traité par lixiviation au début du procédé de lixiviation, puis il a été réduit par un excès de poudre de ferronickel, conduisant à son enrichissement dans le résidu de lixiviation. Environ 50 g/L d'ions Fe ont été éliminés avec succès et précipités sous forme d'hématite contenant 60% de Fe, 0.3% de Ni et 1.5% de S lors d'une précipitation hydrothermale à 200°C pendant 3 h. Grâce à une cristallisation par évaporation à 90°C pendant 8 h, on a obtenu de grosses particules de sulfate de nickel hexahydraté (NiSO 4 ·6H 2 O) contenant 19.4% de Ni, 0.074% de Fe et 10.69% de S. De plus, on a synthétisé, grâce à la cristallisation par congélation à – 8°C pendant 1 h, des particules plus petites du produit NiSO 4 ·6H 2 O contenant 20.3% de Ni, 0.014% de Fe et 11.13% de S.

The Separation and Enrichment of Nickel from Leachate of Nickeliferous Laterite by Using Sulfate Crystallization

Study on the treatment of pyrolysis products from the nitric acid pressure leach liquor of laterite

Separation of nickel and iron from ferronickel via sulfuric acid leaching and hydrothermal precipitation

Separation and Recovery of Iron and Nickel from Low-Grade Laterite Nickel Ore by Microwave Carbothermic Reduction Roasting

Selective Leaching of Valuable Metals from Laterite Nickel Ore with Ammonium Chloride-Hydrochloric Acid Solution

Recovery of nickel and iron from ferronickel powder and high nickel matte via the atmospheric leaching-hematite precipitation process

Efficient Utilization of Limonite Nickel Laterite to Prepare Ferronickel by the Selective Reduction Smelting Process

Mechanism of Calcium Sulphate on the Aggregation and Growth of Ferronickel Particles in the self-Reduction of Saprolitic Nickel Laterite Ore

Electrochemical separation of sulfuric acid from magnesium sulfate solutions: Application for nickel laterite processing

Extraction of ferronickel concentrate from laterite nickel ore by reduction roasting-magnetic separation using spent cathode carbon

Recovery of Pure Co(II) and Ni(II) Solutions from Synthetic Sulfate Leach Liquor of Laterite Ores by Precipitation and Solvent Extraction

Efficient nickel extraction from nickel matte by combined atmospheric-oxygen pressure acid leaching: Thermodynamic analysis and sulfur conversion mechanism

Preparing Ferro-Nickel Alloy from Low-Grade Laterite Nickel Ore Based on Metallized Reduction–Magnetic Separation

Separation of cobalt and nickel from chloride leach solution of nickel laterite ore by solvent extraction

Efficient reductive leaching of valuable elements from oxygen pressure leaching residue of high-grade nickel matte within sulfur dioxide

A novel method: Nickel and cobalt extraction from citric acid leaching solution of nickel laterite ores using oxalate precipitation

Valorization of Solid Residue from the Lateritic Nickel Ore Leaching Process for Ferronickel Production

Extraction of Cu and Ni from Low-Ni Matte by a Combined Chemical Precipitation and Molten Salt Electrolysis Approach

Investigation of leaching of nickel sulfide flotation tailings to recover valuable metals

Selective recovery of nickel from stainless steel pickling sludge with NH3-(NH4)2CO3 leaching system

Eco-friendly and selective separation of nickel and copper from low-grade nickel sulfide ore via sulfur fixation roasting with MgCO 3 followed by sulfuric acid leaching