Improved Electrochemical Properties in the Li3Fe2(PO4)3 by Titanium and Vanadium Doping

Zhengshen Hua,Xin Zhang,Xiaojing Feng,Xiaoran Wang,Jun He,Xin Wang,Huifen Peng

DOI: https://doi.org/10.1016/j.cclet.2018.11.004

IF: 9.1

2018-01-01

Chinese Chemical Letters

Abstract:The nominal Li3-xFe2-xTix(PO4)(2.55)(VO4)(0.45) (x = 0 similar to 0.3) compounds were synthesized by a sol-gel process. Different from the single VO43- doping, further introduction of Ti4+ ion was easy to result in precipitation of a little secondary phases, besides the main NASICON products. The simultaneous substitution of Ti4+ and VO43- for Fe3+ and PO43-, respectively, in the Li3Fe2(PO4)(3) resulted in a net improvement in the rate capability and cycling performance, as compared with the single Ti4+ or VO43--substituted compound. The sample with x = 0.2 presented a high initial discharging capacity of 125.4 mAh/g at the rate of 0.5C, about 25% higher than the Ti4+-substituted Li2.8Fe1.8Ti0.2(PO4)(3), and 102.6 mAh/g after 60 cycles at 2C, about 12% higher than the single VO43--substituted one. The high rate performance between 0.5C to 10C suggested that this sample had a good stability and reversibility. These results proved that the combination of the Ti4+ substitution for Fe3+ with the VO43- substitution for PO43- was a promising method of improving electrochemical performance of the studied Li3Fe2(PO4)(3) cathode material. (C) 2018 Chinese Chemical Society and Institute of Materia Medica, Chinese Academy of Medical Sciences. Published by Elsevier B.V. All rights reserved.