Abstract:Ultra-high toughness cementitious composites (UHTCC) is a kind of cementitious material reinforced by random distributed short fibers, which was proposed by Li and Leung and was designed with micromechanical principles to achieve the strain hardening behavior. This material has potential use in particular environments and structures that experience repeated or fatigue loads. Considering that the fatigue behavior of ultra-high toughness cementitious composites under compression is crucial for its application in certain conditions (e.g. airport runway and road pavements) and fatigue damage of structural components might be affected by both the flexural and compressive fatigue behaviors, the available work is rather limited and a better understanding of the compressive fatigue behavior is required. In this study, a series of monotonic and fatigue tests were performed to investigate the fatigue behavior of this material under compression. Compressive fatigue tests were conducted on 32 cylinder specimens (70 mm in diameter and 140 mm in height). The loading frequency of fatigue tests was set as 4 Hz and the maximum stress was 90%, 85%, 80%, 75%, 70% and 65% of the compressive strength with the stress ratio (the ratio between the minimum fatigue loads to the maximum fatigue load) set constant as 0.1. The S N relationship of ultra-high toughness cementitious composites was given, which indicates that the fatigue life of this material is higher than that of plain concrete and steel fiber reinforced concrete under the same stress level. It is observed that, the specimen failure mode of ultra-high toughness cementitious composites is similar to that of strain softening fiber reinforced concrete. The failure surface and damage process of this material were investigated. A new failure mode of PVA fiber with crush end was discovered with the help of SEM analysis and EDS analysis. This failure mode forms by the ruptured end of fibers experiencing repeated crushing and friction. Besides, based on the various failure modes of PVA fibers, the fatigue failure surface could be divided into three regions, including fatigue source region, transition region and crack extension region. During fatigue failure process, micro cracks initiate in the fatigue source region, propagate in the transition region and form main crack in the crack extension region.

Multiple Impact Resistance of Hybrid Fiber Ultrahigh Toughness Cementitious Composites with Different Degrees of Initial Damage

Experimental Study on Stress Wave Propagation in Ultra High Toughness Cementitious Composites

Anti-explosion Tests and Numerical Simulations of Ultra-High Toughness Cementitious Composites Subjected to Blast by Embedded Explosives

MULTIPLE IMPACT COMPRESSIVE PROPERTIES AND CONSTITUTIVE MODEL OF ULTRA-HIGH TOUGHNESS CEMENTITIOUS COMPOSITES

Bending Fatigue Properties of Ultra-High Toughness Cementitious Composite (UHTCC)

A novel damage evaluation method for ultra‐high‐performance fiber reinforced concrete under multiple impact loads

Influence of Hybrid Fibers on Flexural Properties of Ultra High Toughness Cementitous Composites with Nano-SiO2

Mesoscale Numerical Investigation of Dynamic Spalling Fracture in Toughness Concrete

Tensile and Flexural Properties of Ultra High Toughness Cemontious Composite

Effects of Steel Fiber and Target Thickness on the Penetration Resistance of UHPC under High Velocity Small Projectile Impact Loading

Contribution of Steel Fiber on the Dynamic Tensile Properties of Hybrid Fiber Ultra High Toughness Cementitious Composites Using Brazilian Test

Mechanical Characterization and Impact Damage Assessment of Hybrid Three-Dimensional Five-Directional Composites

Influence of Steel Fiber on Dynamic Compressive Behavior of Hybrid Fiber Ultra High Toughness Cementitious Composites at Different Strain Rates

Tensile behavior of ultra‐high performance concrete reinforced with different hybrid fibers

Investigation on Compressive Fatigue Damage Process of Ultra-High Toughness Cementitious Composites

Low-velocity impact response of 3D woven hybrid epoxy composites with carbon and heterocyclic aramid fibres

Toughness evaluation of ultra-high toughness cementitious composite specimens with different depths

Low‐velocity impact properties of carbon fiber/ultrahigh molecular weight polyethylene fiber hybrid composites

Tensile Behavior of Hybrid Fiber-Reinforced Ultra-High-Performance Concrete

Study of the dynamic response and damage evolution of carbon fiber/ultra-thin stainless-steel strip fiber metal laminates under low-velocity impact

EXPERIMENTAL STUDY ON SPALL BEHAVIOR OF ULTRA-HIGH TOUGHNESS CEMENTITIOUS COMPOSITES