Preparation of Gelatin/Carrageenan Blend Film and Reinforced by Bagasse Hemicelluloses Extracted by Liquid Hot Water

Chengrong Qin,Cheng Wang,Baojie Liu,Lingzhi Huang,Chen Liang,Shuangquan Yao
DOI: https://doi.org/10.1166/jbmb.2019.1818
2019-01-01
Journal of Biobased Materials and Bioenergy
Abstract:The polymer-blend films (PBFs) have the potential to be utilized as packaging material for enhancing food shelf life. But the most important factor restricting the application is low mechanical strength. Recycling hemicellulose can be used as a new value-added product to increase economic efficiency. In this paper, bagasse hemicellulose was extracted by pH pre-controlled hot water extraction. Its utilization in the reinforcement of a gelatin/carrageenan PBFs was studied. The effect of reaction parameters on the tensile strength (TS) and elongation at break (EAB) of PBFs was studied. The most important reaction parameter was hemicellulose dosage. The optimum preparation process of PBFs was determined by the response surface analysis method. The optimum reaction conditions of TS was 34.84 degrees C, glycerin dosage 1.43%, hemicellulose dosage 0.92%, TS was 54.19 MPa. The optimum reaction conditions of EAB was 34.92 degrees C, glycerin dosage 1.45%, hemicellulose dosage 0.87%, EAB was 26.42%. The results provide theoretical support for the application of hemicellulose in food packaging.
What problem does this paper attempt to address?