Abstract:Edible coatings have attracted the attention of researchers in recent years due to their degradability, safety, non-toxicity, low cost, good preservation effect, and other advantages. To prepare a new edible film with good mechanical and barrier properties, carboxymethyl chitosan (CMCS) and gelatin (GL) were selected as the film-forming matrix in this experiment, and glycerol, CaCl2, Tween-20, and ascorbic acid (AA) have been added as plasticizers, crosslinking agents, surfactants, and antioxidants. Crosslinking agents and antioxidants first, the film was prepared by the casting method, and single factor tests were used to compare the effects of different CMCS: GL (w:w), glycerol, CaCl2, Tween-20, and AA on mechanical properties (Tensile Strength (TS), Elongation at break (EAB)) and barrier properties (Water Vapor Permeability (WVP), Oxygen Permeability (OP)). Then, the weighting of each performance index is determined by a combination of principal component analysis and the comprehensive membership evaluation method. The formula for calculating the overall rating of edible film performance was determined. Finally, the manufacturing process of edible film with better performance was optimized by a response surface test. The results showed that the influence of each factor on the performance of the edible film was as follows: Glycerol addition > CaCl2 addition > CMCS:GL, Tween-20, and AA had no significant influence on the performance of the edible film. When calculating the overall edible film property score, the weights of TS, EAB, WVP, and OP were 0.251, 0.068, 0.334, and 0.347, respectively. The optimal formulation for an edible film based on CMCS-GL with better properties than pure CMCS and GL film was CMCS:GL = 2:1, with the addition of 1% glycerol, 2% CaCl2, 0.1% Tween-20, and 2% AA. The TS, EAB, OP, and WVP of the film obtained with this formula were: 16.28 MPa, 71.46%, 1.39 × 10−12 g·cm/(cm2·s·Pa), 5.10 × 10−11 cm3·cm/(m2·s·Pa), respectively. This study suggests that CMCS-GL-based edible coatings can be used as a new food packaging material.
What problem does this paper attempt to address?
Based on the provided text content, the main problem that this paper attempts to solve is:
**Optimizing the mechanical and barrier properties of carboxymethyl chitosan - gelatin - based edible films.**
Specifically, the researchers selected carboxymethyl chitosan (CMCS) and gelatin (GL) as film - forming substrates, and added glycerol, calcium chloride (CaCl₂), Tween - 20, and ascorbic acid (AA) as plasticizers, cross - linking agents, surfactants, and antioxidants. Through single - factor experiments, the effects of different CMCS:GL ratios, glycerol, CaCl₂, Tween - 20, and AA on the mechanical properties (tensile strength (TS), elongation at break (EAB)) and barrier properties (water vapor permeability (WVP), oxygen permeability (OP)) of the films were compared. Then, combined with principal component analysis and comprehensive membership degree evaluation methods, the weights of each performance index were determined, and the overall scoring formula for the performance of the edible films was determined. Finally, the preparation process of the edible films with good performance was optimized through response surface testing.
The research results show that the order of the influence of various factors on the performance of the edible films is: the amount of glycerol added > the amount of calcium chloride added > CMCS:GL ratio, while Tween - 20 and AA have no significant influence on the film performance. When calculating the overall performance score of the edible films, the weights of TS, EAB, WVP, and OP are 0.251, 0.068, 0.334, and 0.347 respectively. The finally determined optimal formula is CMCS:GL = 2:1, with 1% glycerol, 2% CaCl₂, 0.1% Tween - 20, and 2% AA added. The TS, EAB, OP, and WVP of the films prepared using this formula are 16.28 MPa, 71.46%, \(1.39\times10^{-12}\text{g·cm/(cm}^2\text{·s·Pa)}\) and \(5.10\times10^{-11}\text{cm}^3\text{·cm/(m}^2\text{·s·Pa)}\) respectively.
This research shows that the CMCS - GL - based edible coating can be used as a new food packaging material.