Enhancement of Mechanical and Barrier Property of Hemicellulose Film via Crosslinking with Sodium Trimetaphosphate

Yuelong Zhao,Hui Sun,Biao Yang,Baomin Fan,Huijuan Zhang,Yunxuan Weng

DOI: https://doi.org/10.3390/polym13060927

IF: 5

2021-03-17

Polymers

Abstract:Hemicellulose is a kind of biopolymer with abundant resources and excellent biodegradability. Owing to its large number of polar hydroxyls, hemicellulose has a good barrier performance to nonpolar oxygen, making this biopolymer promising as food packaging material. Hydrophilic hydroxyls also make the polymer prone to water absorption, resulting in less satisfied strength especially under humid conditions. Thus, preparation of hemicellulose film with enhanced oxygen and water vapor barrier ability, as well as mechanical strength is still sought after. Herein, sodium trimetaphosphate (STMP) was used as esterification agent to form a crosslinked structure with hemicellulose through esterification reaction to render improved barrier performance by reducing the distance between molecular chains. The thus modified hemicellulose film achieved an oxygen permeability and water vapor permeability of 3.72 cm3 × μm × m−2 × d−1 × kPa−1 and 2.85 × 10−10 × g × m−1 × s−1 × Pa−1, respectively, at the lowest esterification agent addition of 10%. The crosslinked structure also brought good mechanical and thermal properties, with the tensile strength reaching 30 MPa, which is 118% higher than that of the hemicellulose film. Preliminary test of its application in apple preservation showed that the barrier film obtained can effectively slow down the oxidation and dehydration of apples, showing the prospect of application in the field of food packaging.

polymer science

What problem does this paper attempt to address?

The problems that this paper attempts to solve are: to improve the mechanical and barrier properties of hemicellulose films by using a green cross - linking agent - Sodium Trimetaphosphate (STMP). Specifically, the research aims to:

1. **Improve oxygen and water vapor barrier properties**: Due to its abundant polar hydroxyl groups, hemicellulose has good non - polar oxygen barrier properties, but these hydroxyl groups also make it easy to absorb water, resulting in insufficient strength under humid conditions. Therefore, it is necessary to improve the oxygen and water vapor barrier properties of hemicellulose films.

2. **Enhance mechanical strength**: Reduce the distance between molecular chains through cross - linking reactions, thereby increasing the mechanical strength of the film.

3. **Ensure safety and edibility**: Select STMP as a cross - linking agent because it is a commonly used food additive, non - toxic and edible, and suitable for the safety requirements of food packaging materials.

### Specific objectives
- Prepare hemicellulose films with enhanced oxygen and water vapor barrier properties and mechanical strength.
- Study the effects of different STMP addition amounts on film properties.
- Evaluate the performance of the modified hemicellulose films in practical applications, such as apple preservation experiments.

### Experimental methods
- Use STMP to carry out esterification reactions with hemicellulose to form a cross - linked structure.
- Add sorbitol as a plasticizer and polyvinyl alcohol (PVA) as an enhancer and co - substrate.
- Prepare a series of films by solution casting method and test their mechanical, thermal, barrier properties and wettability.

### Main results
- When the addition amount of STMP in the modified hemicellulose film is 10%, the oxygen permeability and water vapor permeability reach the lowest values respectively: 3.72 cm³×µm×m⁻²×d⁻¹×kPa⁻¹ and 2.85×10⁻¹⁰ g×m⁻¹×s⁻¹×Pa⁻¹.
- The tensile strength of the film reaches 30 MPa, which is 118% higher than that of the unmodified hemicellulose film.
- Apple preservation experiments show that the modified film can effectively slow down the oxidation and dehydration of apples, showing application prospects in the field of food packaging.

Through the above research, the paper demonstrates the potential of STMP - cross - linked hemicellulose films in improving barrier properties and mechanical strength, and verifies their feasibility in practical applications.