Abstract:Given multiple material performance advantages, ceramic matrix composite (CMC) material has become one of the most promising hot structural materials used for thermal protection system in hypersonic vehicles. Under harsh thermal exposure of vehicles in flight, the design of connection structure would be a critical issue in improving load-carrying efficiency and ensuring service safety of aircraft structures in service environments. However, little attention was paid on mechanical behavior and its factors affecting the mechanical property of CMC joining at elevated temperature. To address this concern, a 3D finite element model coupled with progressive damage analysis is carried out to predict high temperature tensile properties and failure behavior of single-lap, double-bolt CMC/superalloy joints assembled by two serial protruding-head bolts. In the implementation of progressive damage analysis of 2D plain-woven C/SiC composites, a user-defined subroutine UMAT including a nonlinear constitutive model, 3D Alvaro failure criterion and Tan's material degradation rule were embedded into the general package ABAQUS® through Fortran program interface. A parametric study considering geometries of joints was performed to evaluate their resultant influence on high temperature tensile behavior and the associated damage mechanisms for the CMC/superalloy double-bolt joint. New findings were provided for full exploitation of high performance through geometric design of ceramic matrix composite hot structure for hypersonic aircraft.

Evolution and characterization of cyclic thermal shock-induced thermomechanical damage in oxide/oxide ceramics matrix composites

Representation of Micro-Structural Evolution and Thermo-Mechanical Damage in Thermal Shocked Oxide/oxide Ceramic Matrix Composites

Micro-porosity As Damage Indicator for Characterizing Cyclic Thermal Shock-Induced Anisotropic Damage in Oxide/oxide Ceramic Matrix Composites

Damage Modeling of Oxide/oxide Ceramic Matrix Composites under Cyclic Loading Conditions

A micromechanical damage model for oxide/oxide ceramic matrix composites with hierarchical porosity under thermomechanical loading

Constitutive model and failure criterion for orthotropic ceramic matrix composites under macroscopic plane stress

Thermomechanical fatigue damage development of continuous carbon fiber-reinforced ceramic-matrix composites subjected to different loading sequences and phase angles

Development and validation of damage and failure models for the design of ceramic matrix composite components

Experimental and numerical analysis of CMCs mechanical properties under high-temperature thermal gradient environment

Damage Analysis of a SiCf/SiC Ceramic Matrix Composite under Stepwise Fatigue Loading with Acoustic Emission

Modeling Multiple-Step Loading Damage Evolution in Continuous Fiber-Reinforced Ceramic-Matrix Composites at Room and Elevated Temperatures

Damage and failure analysis of a SiCf/SiC ceramic matrix composite using digital image correlation and acoustic emission

Characterisation and damage modelling of oxide/oxide composites considering temperature dependence

Damage of Short-Fiber-Reinforced Metal Matrix Composites Considering Cooling and Thermal Cycling

Modeling Tensile Damage and Fracture Behavior of Fiber-Reinforced Ceramic-Matrix Minicomposites

Effect of interface damage on tensile behavior of fiber-reinforced ceramic-matrix composites after thermal fatigue loading

High Temperature Fatigue Assessment of a SiCf/SiC Ceramic Matrix Composite Using Advanced Monitoring Techniques

Parametric Influences of Geometric Dimensions on High Temperature Mechanical Behaviors and Damage Mechanisms of Ceramic Matrix Composite and Superalloy Double Bolted Joints

A temperature-dependent constitutive model for fiber-reinforced ceramic matrix composites and structural stress analysis

Computational Micromechanics for High-Temperature Constitutive Equations of Polymer-Matrix Composites With Oxidation Reaction, Damage, and Degradation

Relationship between hysteresis loops and cracking evolution/closure in ceramic-matrix composites under tension-tension fatigue loading