Unveiling the Microstructure Evolution and the Short-Time Tensile Creep Behavior in the CuCrZr Alloy
Yihao Luo,Xiao Liu,Liuyi Huang,Youliang Wu,Shihong Zhao,Hang Zhang,Gaofeng Yu,Min Liu,Junjing He,Jiabin Liu,Youtong Fang
DOI: https://doi.org/10.1016/j.matchar.2024.114305
IF: 4.537
2024-01-01
Materials Characterization
Abstract:The creep behavior of the CuCrZr alloy, used in the combustion chamber wall of reusable launch vehicles, was investigated at 600-700 K and 150-250 MPa. Results demonstrate significant differences in the creep behavior, microstructure evolution including texture component, dislocation configurations and cavities at 600 K and 700 K, particularly at 250 MPa. At 600 K, the creep life exceeds 400 h, while at 700 K it drops below 0.5 h. The texture components evolved at 600 K-250 MPa are more balanced between hard texture (Brass texture) and soft texture (Goss texture and R-Goss texture). The texture components at 700 K-250 MPa are integrally biased toward the soft texture, implying that it is favorable to accelerate creep strain. The introduced high-density dislocations before creep act as an effective barrier to impede the motion of dislocations at 600 K, inducing longtime dynamic balance of work hardening and recovery softening, while the pre-creep dense dislocations act as an energy supplement at 700 K, promoting that recovery softening dominates the creep process. The dense dislocations can provide energetic support for cavity nucleation.