The Corrosion Behavior of Porous Ni–Cr–Fe Alloy in 2 Mol L−1 Alkaline Solution

Liang Wu,Xiaona Li,Ge Yang,Zhi Tang,Xiaohua Guo,Yang Xu,Yifeng Xiao,Jinwen Qian,Yanfei Xu,Yuehui He
DOI: https://doi.org/10.3139/146.111712
2018-01-01
International Journal of Materials Research
Abstract:Ni-Cr-Fe alloy samples with different porosities were prepared via the Kirkendall effect, with a reactive synthesis of Ni, Cr, and Fe elemental powders. The microstructure, surface morphology and the compositions were analyzed with X-ray diffraction and scanning electron microscopy. The corrosion behavior was explored in a 2 mol L-1 KOH solution using electrochemical methods and an immersion test. The polarization resistance indicated that the free corrosion potential and the lower corrosion current of the porous Ni- Cr-Fe alloy were -0.18528 V and 3.5998 x 10(-7) A cm(-2). The immersion test showed that after 25 days of immersion, the weight change of porous Ni-Cr-Fe alloy was 0.132 %, which was less than the porous Ni (0.346 %). X-ray photoelectron spectroscopy results revealed the corrosion products of the porous Ni-Cr-Fe alloy and the porous Ni. The corrosion mechanism of the porous Ni-Cr-Fe alloy was discussed.
What problem does this paper attempt to address?