Abstract:This work examines the performance of composite panels when subjected to underwater impulsive loads. The scaled fluid–structure experimental methodology developed by Espinosa and co-workers was employed. Failure modes, damage mechanisms and their distributions were identified and quantified for composite monolithic and sandwich panels subjected to typical blast loadings. The temporal evolutions of panel deflection and center deflection histories were obtained from shadow Moiré fringes acquired in real time by means of high speed photography. A linear relationship of zero intercept between peak center deflections versus applied impulse per areal mass was obtained for composite monolithic panels. For composite sandwich panels, the relationship between maximum center deflection versus applied impulse per areal mass was found to be approximately bilinear but with a higher slope. Performance improvement of sandwich versus monolithic composite panels was, therefore, established specially at sufficiently high impulses per areal mass (I0/M¯>170ms−1). Severe failure was observed in solid panels subjected to impulses per areal mass larger than 300ms−1. Extensive fiber fracture occurred in the center of the panels, where cracks formed a cross pattern through the plate thickness and delamination was very extensive on the sample edges due to bending effects. Similar levels of damage were observed in sandwich panels but at much higher impulses per areal mass. The experimental work reported in this paper encompasses not only characterization of the dynamic performance of monolithic and sandwich panels but also post-mortem characterization by means of both non-destructive and microscopy techniques. The spatial distribution of delamination and matrix cracking were quantified, as a function of applied impulse, in both monolithic and sandwich panels. The extent of core crushing was also quantified in the case of sandwich panels. The quantified variables represent ideal metrics against which model predictive capabilities can be assessed.

Blast response of water-backed metallic sandwich panels subject to underwater explosion – Experimental and numerical investigations

Experimental and numerical investigation on the anti-penetration performance of metallic sandwich plates for marine applications

Blast Resistance of Metallic Sandwich Panels Subjected to Proximity Underwater Explosion

Dynamic Responses Of Ultralight All-Metallic Honeycomb Sandwich Panels Under Fully Confined Blast Loading

A Novel Efficient Method to Evaluate the Dynamic Response of Laminated Plates Subjected to Underwater Shock

Dynamic response of laser-welded corrugated sandwich panels subjected to plane blast wave

Dynamic response of hybrid corrugated/foam sandwich structure under combined loading of blast and fragments

Dynamic behavior of aluminum honeycomb sandwich panels under air blast: Experiment and numerical analysis

Blast responses of steel stiffened panels subjected to plane shock waves

Numerical analysis of the damage on Ⅰ-core sandwich panels subjected to combined blast and fragment loading

Experimental study on failure mechanisms of sandwich panels with multi-layered aluminum foam/UHMWPE laminate core under combined blast and fragments loading

Centrifuge Experiment and Numerical Analysis of an Air-Backed Plate Subjected to Underwater Shock Loading

An analytical method for evaluating the dynamic response of plates subjected to underwater shock employing Mindlin plate theory and Laplace transforms

Three-dimensional numerical modeling of composite panels subjected to underwater blast

Contact underwater explosion response of metallic sandwich panels with different face-sheet configurations and core materials

Experimental and Numerical Study on Dynamic Response of Foam-Nickel Sandwich Panels under Near-Field Blast Loading

The Fluid-Solid Interaction Dynamics between Underwater Explosion Bubble and Corrugated Sandwich Plate

Failure Mechanisms in Composite Panels Subjected to Underwater Impulsive Loads

A New Blast Absorbing Sandwich Panel with Unconnected Corrugated Layers—Numerical Study

Experimental investigation into the synergetic damage of foam-filled and unfilled corrugated core hybrid sandwich panels under combined blast and fragment loading

Dynamic response of composite sandwich structures with the honeycomb-foam hybrid core subjected to underwater shock waves: Numerical simulations