Microstructures and electrical properties of (1-x)Li0.5Sm0.5TiO3–xNa0.5Bi0.5TiO3 ceramics

Xiao Liu,Changlai Yuan,Fenghua Luo,Xinyu Liu,Guohua Chen,Changrong Zhou

DOI: https://doi.org/10.1016/j.matchemphys.2018.10.040

IF: 4.778

2019-01-01

Materials Chemistry and Physics

Abstract:A-site (Li0.5Sm0.5)2+ substitutions for (Na0.5Bi0.5)2+ of Na0.5Bi0.5TiO3 ceramics were prepared by the conventional solid-state reaction. Structural and electrical properties, including ferroelectric, dielectric, and impedance attributes of the as-prepared ceramics were studied systematically. The new solutions, (1–x)Li0.5Sm0.5TiO3–xNa0.5Bi0.5TiO3, could be roughly separated into three groups in accordance with their electrical polarity as microwave dielectric (x < 0.6), relaxor ferroelectric (0.6 ≤ x ≤ 0.92), and ferroelectric (x > 0.92). An increase in (Na0.5Bi0.5)2+ content had a positive impact on the ferroelectric and dielectric properties. Compositions closest to zero temperature coefficient of resonant frequency(τf) were obtained at x = 0.4, where permittivity(εr) was 154 and the microwave quality factor, Q × f was 1560 GHz for the samples sintered at 1125 °C. The highest discharged energy density of 0.92 J/cm3 was achieved at x = 0.9. The loss of Bi3+ during sample processing changed the conductive mechanism from electronic conduction to oxide ion conduction, thus presenting a way to optimize the compositions with various donor and acceptor dopants for better performance in microwave and ferroelectric ceramics.