Improved ferroelectricity of (1−x)Na0.5Bi0.5TiO3–xBaTiO3 ceramics rapidly sintered at low temperature

Xijun Xu,Jinguo Jiang,Hussain Ahmad,Guoliang Yuan,Jiang Yin,Zhiguo Liu

DOI: https://doi.org/10.1016/j.ceramint.2014.04.014

IF: 5.532

2014-01-01

Ceramics International

Abstract:High insulating (1−x)Na0.5Bi0.5TiO3–xBaTiO3 (x=0–0.08) ceramics were rapidly sintered at low temperature and then enhanced polarizations were observed. (1−x)Na0.5Bi0.5TiO3–xBaTiO3 nano-powders were prepared by the sol–gel method and then their ceramics were rapidly sintered at 920–1150°C. According to the saturated ferroelectric hysteresis loops, the acquired saturated and remnant polarizations are ~48μC/cm2 and ~40μC/cm2 at x=0.03–0.08, and the coercive electric field decreases from ~70kV/cm of pure Na0.5Bi0.5TiO3 to ~30kV/cm at x=0.06–0.08. Furthermore, the piezoelectric d33 is 166.8pC/N at x=0.06, where the morphotropic phase boundaries occur. These improved properties are achieved because the leakage current is reduced through compressing the loss of Na and Bi components during ceramics׳ preparation process.