Abstract:In order to achieve well-performing chemical strengthening behavior, the composition of 86.12(xSiO(2)-yAl(2)O(3)-zP(2)O(5))- 9.95Na(2)O- 1.27ZnO- 2.66Li(2)O (x = 55-85wt%, y = 10-40wt% and z = 5-35wt%) were prepared by conventional melt-quenching technique. The glass forming region was obtained. Two compositional series of 65SiO(2)-yAl(2)O(3)-zP(2)O(5) (15 <= y <= 30, 5 <= z <= 30, 5 <= z <= 20) (Series I) and xSiO(2)-20%Al2O3-zP(2)O(5) (60 <= x <= 75, 5 <= z <= 20) (Series II) have been investigated. The relationship between glass structure and composition was investigated. The results show that the transparent and homogeneous glass is formed when the glass former P2O5 is lower than or equal to 15 wt% roughly. The P2O5 substitution for Al2O3 accelerates the depolymerization of aluminosilicate network. Phosphorus acts as network formers in the form of P-1 and P-2 units. In the case of the P2O5 substitution for SiO2, the roles of phosphorus in the glass network include P-0, P-1, P-2 and P-3 units. Furthermore, the Series I and Series II glass samples were chemical strengthened. The ion-exchange depth and the elastic modulus before and after chemical strengthening were studied. The results reveal that the ion exchange depth and elasticity modulus after chemical strengthening is maximum at 64 mu m and 80.5 GPa for x/z = 5.4 sample, respectively. The addition of phosphorus accelerates ion exchange, which is mainly attributed to the formation of ion channels. The number of P-n and the coordination number of phosphorus are the main factors effecting the ion channels.

Roles Of P2o5 Addition On The Viscosity And Structure Of Cao-Sio2-Al2o3-Na2o-P2o5 Melts

Roles of P<sub>2</sub>O<sub>5</sub> Addition on the Viscosity and Structure of CaO–SiO<sub>2</sub>–Al<sub>2</sub>O<sub>3</sub>–Na<sub>2</sub>O–P<sub>2</sub>O<sub>5</sub> Melts

FTIR, Raman and NMR Investigation of CaO–SiO2–P2O5 and CaO–SiO2–TiO2–P2O5 Glasses

Effect Of P2o5 Addition On The Viscosity And Structure Of Titanium Bearing Blast Furnace Slags

The Role of Phosphate in the Glass Forming Region, Structure and Mechanical Properties for the SiO2-Al2O3-P2O5 System Contains High-Aluminum

Effect of P2O5 on Nucleation, Crystallization and Mechanical Properties of Y2O3–Al2O3–SiO2 Glasses

Effect of P 2 O 5 on Nucleation, Crystallization and Mechanical Properties of Y 2 O 3-Al 2 O 3-Sio 2 Glasses

Structure, Glass Stability And Rheological Properties Of Na2o-Cao-Al2o3-Sio2 Glasses Doped With Y2o3

Effect of La2O3 and FexO on the viscosity and structure of CaO–MgO–Al2O3–SiO2 melts

Effect of P<SUB>2</SUB>O<SUB>5</SUB> on evolution of microstructure of MgO–Al<SUB>2</SUB>O<SUB>3</SUB>–SiO<SUB>2</SUB> glass ceramics

Crystallization behavior of MgO-Al2O3-SiO 2-P2O5 glass-ceramics

Understanding the Relationship Between Structure and Thermophysical Properties of CaO-SiO 2 -Mgo-al 2 O 3 Molten Slags

A Modified Random Network Model for P2O5–Na2O–Al2O3–SiO2 Glass Studied by Molecular Dynamics Simulations

The Influences of P2O5 Addition on Crystallization Mechanism of Mica Glass-Ceramics

Effect of La2O3 on the viscosity and structure of CaO–SiO2(–Al2O3)–La2O3 melts

Insights into the Iron- and Phosphorus-Induced Structural Rearrangements in Sodium Aluminoborosilicate Glasses and Their Impact on Melt Rheology and Crystallization Behavior

Effect of P2O5 on Crystallization and Foaming of Wollastonite Based Foam Glass Ceramics

Role of Na2O and TiO2 on viscosity and structure of Sodium-Titanium-bearing slag

Effects of P 2 O 5 on Sinterability, Microstructures and Properties of Glass/alumina Composites

Structure, thermal stability and spinnability of the CaO-MgO-Al2O3-SiO2 glasses with SiO2 replaced by Al2O3

Investigation of the Viscosity and Structural Properties of CaO-SiO 2 -TiO 2 Slags