Investigation of the Viscosity and Structural Properties of CaO-SiO 2 -TiO 2 Slags

Kai Zheng,Zuotai Zhang,Lili Liu,Xidong Wang

DOI: https://doi.org/10.1007/s11663-014-0053-8

2014-01-01

Abstract:The viscosity of CaO-SiO 2 -TiO 2 slags was measured via the rotating cylinder method to reveal the effect of TiO 2 on viscous flow of the slags. Furthermore, the structure of the ternary slags and the role of Ti 4+ were investigated by Fourier transform infrared and Raman spectroscopy techniques. The results are beneficial for a better understanding of the behaviors of Ti-bearing silicate slags. The TiO 2 additions lowered the viscosity and apparent activation energy of the slags. However, the degree of polymerization (DOP) of silicate network was found to be enhanced with increasing the TiO 2 content, which is suggested by the increase in mole fraction of Q 3 ([SiO 4 ]-tetrahedra with three bridging oxygens) and the decrease in Q 0 . The Eq. [2] Q 2 ↔ Q 1 + Q 3 was appropriate to express the relationship of different Q n species. The introduction of Ti 4+ into the silicate network as network formers increased the DOP but weakened the strength of slag structure at the same time. Besides, a large proportion of Ti 4+ exists in the slag in the form of TiO_4^4 - monomers, resulting in a decrease of viscosity with increasing TiO 2 content.