Abstract:In the current work, the bulk (1-x) Bi0.5Na0.5TiO3-xCaTiO(3) [BNCT100x] system was synthesized via solid-state route. CaTiO3 in solid solution with Bi0.5Na0.5TiO3 was observed to decrease the dielectric constant at higher temperature and raise the dielectric constant at lower temperature. Polarization hysteresis measurements indicated that the ferroelectricity of Bi0.5Na0.5TiO3 was weakened with an increase of CaTiO3, resulted in the shift of the depolarization temperature (T (d)) toward lower temperatures. X-ray diffraction analysis revealed that TiO2 was produced as a secondary phase due to the losses of Bi and Na during milling and sintering processes. Moreover, the addition of Ca promoted the segregation of Ti out of BNT grains. Dielectric properties of BNCT12 ceramics with different dopant levels of Mn were characterized as a function of temperature for potential use of high-temperature capacitors. Modification of BNCT12 materials with Mn improved the temperature characteristic of capacitance (-55A degrees C to 250A degrees C, a-C-3/C-25A degrees C a parts per thousand currency sign +/- 15%). Finally, by doping 1.5 wt% Mn, the dielectric constant at room temperature could reach over 900, with a low dielectric loss below 1% and a high insulation resistivity about 10(12) Omega aEuro cent cm. Furthermore, a small amount of Mn influenced the microstructure in the way to inhibit the long grains and grain growth of BNCT solution ceramics. However, excess Mn caused abnormal grain growth, and therefore, rectangle grains appeared again.

High Temperature Stable Dielectric Properties and Enhanced Energy-Storage Performance of (1− X)(0.85na0.5bi0.5tio3 − 0.15ba0.8ca0.2ti0.8zr0.2o3)− Xk0.5na0.5nbo3 Lead-Free Ceramics

Enhanced Energy-Storage Performance and Temperature-Stable Dielectric Properties of (1-X)[(na0.5bi0.5)0.95ba0.05]0.98la0.02tio3-xk0.5na0.5nbo3 Lead-Free Ceramics

Temperature‐stable Na 0.5 Bi 0.5 TiO 3 ‐based Ceramics with Favorable Low‐temperature Dielectric and Energy Storage Property

High Energy Storage Properties and Dielectric Temperature Stability of (1-X)(0.8bi0.5na0.5tio3-0.2ba0.3sr0.7tio3)-xnanbo3 Lead-Free Ceramics

Dielectric Properties of (bi0.5k0.5)zro3 Modified (k0.5na0.5)nbo3 Ceramics As High-Temperature Ceramic Capacitors

Super-stable Permittivity and Low Dielectric Loss of (1-X) Na0.5Bi0.5+yTiO3-xNaTaO3 Ceramics Within an Ultra-Wide Temperature Range

Enhanced energy-storage performance and temperature-stable dielectric properties of (1 − x )(0.94Na 0.5 Bi 0.5 TiO 3 –0.06BaTiO 3 )– x Na 0.73 Bi 0.09 NbO 3 ceramics

High-temperature Dielectrics Based on 0.95(0.94Bi0.5na0.5tio3-0.07Bialo3)-0.05k0.5na0.5nbo3

TEMPERATURE-INDEPENDENT DIELECTRIC PROPERTIES OF 0.82[0.94bi0.5na0.5tio3–0.06batio3]–0.18k0.5na0.5nbo3 CERAMICS

Excellent High-Temperature Dielectric Stability of BNT-based Ceramics Modified by NaNbO3

Temperature-stable Na0.5Bi0.5TiO3-based Relaxor Ceramics with High Permittivity and Large Energy Density under Low Electric Fields

Superior Thermal Stability and Energy Storage Properties of (1-X)na0.3bi0.3ba0.04sr0.36tio3-xznta2o6 Lead-Free Ceramic

High Temperature Stable Dielectric Properties of (k0.5na0.5)0.985bi0.015nb0.99cu0.01o3 Ceramics with Core–shell Microstructures

High-temperature dielectric properties of Bi0.5Na0.5TiO3–NaNbO3–Sr0.8Na0.4Nb2O6 ceramics

Enhanced Energy-Storage Properties of (1−x)[(1−y)(bi0.5na0.5)tio3–y(bi0.5k0.5)tio3]–x(k0.5na0.5)nbo3 Lead-Free Ceramics

High-temperature stable dielectrics in Mn-modified (1-x) Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-xCaTiO<sub>3</sub> ceramics

Excellent Thermal Stability and Energy Storage Properties of Lead‐free Bi0.5Na0.5TiO3‐based Ceramic

Superior energy storage properties in (1-x)(0.65Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.35Bi<sub>0.2 </sub>Sr<sub>0.7</sub>TiO<sub>3</sub>)-xCaZrO<sub>3</sub> ceramics with excellent temperature stability

Ultrahigh energy storage performance of a 0.75Bi0.47Na0.47Ba0.06TiO3-0.25CaTi0.8Sn0.2O3 ceramic under moderate electric fields

Enhancement of Charge-Discharge Properties and Temperature Stability of (Ba0.975Na0.05)Ti0.99Nb0.01O3 Ceramic by Doping High-Entropy Oxide