Temperature‐stable Na 0.5 Bi 0.5 TiO 3 ‐based Ceramics with Favorable Low‐temperature Dielectric and Energy Storage Property

Yingchun Su,Xuefan Zhou,Guoliang Xue,Hang Luo,Dou Zhang

DOI: https://doi.org/10.1111/jace.19029

IF: 4.186

2023-01-01

Journal of the American Ceramic Society

Abstract:In this work, (1 - x)(0.94Na(0.5)Bi(0.5)TiO(3)-0.06BaTiO(3))-xKTaO(3) (x = 0-0.30) ceramics are developed for dielectric capacitor applications. The introduction of KTaO3 from x = 0 to 0.30 increases the tolerance factor t from 0.984 to 1.005 and causes the decrease of ferroelectric rhombohedral phase in the ceramics. Besides, a gradual structural change toward a higher symmetry can be detected, accompanied by the obvious domain refinement. In the aspect of electrical property, the strengthened dielectric relaxation leads to the greatly enhanced thermal stability of dielectric response. The decline in T-s from 98 to -96? causes a significant widening of the low-temperature region with temperature-stable dielectric constant epsilon(r) and low dielectric loss tan delta. The x = 0.30 ceramic shows a high epsilon(r) (25?) of 1094 with the temperature coefficient of capacitance <=+/- 15% over -70 to 200?, which exceeds the X9R standard. Meanwhile, tan delta is less than 0.02 in a wide temperature range of -35 to 300?. In addition, the ultrafine grain size of 290 nm, large bandgap of 3.22 eV, and high resistance of the x = 0.30 ceramic contribute to its electrical breakdown strength. A linear-like P-E loop with the large discharged energy density W-D similar to 3.50 J/cm(3) and high energy efficiency eta similar to 90.1% is obtained under 28 kV/mm at room temperature. The thermal stability of the energy storage performance is also satisfactory with the variation of W-D less than 15% over -40 to 200?, and the eta is higher than 85%.