Abstract:Textile reinforced concrete (TRC) is a type of composite material with great potential in lightweight and thin-walled structural components bearing high capacity. In this study, TRC thin-plates with epoxy resin impregnated fibre (type 1) and non-impregnated fibre (type 2) were exposed to high temperatures from 35 degrees C to 800 degrees C with the unstressed residual test method. The processed TRC thin-plates were examined through four-point bending tests with the aim of building a foundation for a fire prevention code for TRC. The results demonstrate that the ultimate load of type 1 TRC thin-plates is relatively high and does not vary significantly when the target temperature is below 200 degrees C. The ultimate load of type 2 TRC thin-plates is lower than that of type 1, and does not vary significantly when the target temperature is below 400 degrees C; the turning point for the reduction of ultimate load is 400-500 degrees C, and 20% of loading capacity at normal temperature is maintained at 800 degrees C. Stripping damage to type 1 occurs along the interface and the damage is brittle. For a target temperature of 300 degrees C, epoxy resin is prone to deteriorate and the bursting ratio of the specimens was 100%. The damage feature of type 2 thin-plates is a slipping failure between fibre and mortar mixes, and significant ductile damage properties were observed during the damage process. The investigations were also accompanied by scanning electron microscope and alpha ray spectrometer analyses, which provided an additional basis for analysing the damaged sections of specimens. The results show that the surface flaws of the carbon filaments, matrix decomposition and the weak bond behaviour between the fibres and matrix are affected by elevated temperatures. These three factors may result in the decline of the bearing capacity of type 2 TRC thin-plates.

Effects of Strain Rate and Temperature on the Flexural Behavior of Basalt and Glass Textile–Reinforced Concrete

Experimental Study of Mechanical Properties of CFRP under Different Strain Rates and Temperatures

Flexural Behavior of TRC Contained Chopped Fibers Subjected to High Temperature

Flexural behavior of concrete-filled circular steel tubes under high-strain rate impact loading

Flexural response of TRM subjected to low-velocity impact loads: Experimental and analytical study

Effectiveness of TRC Jackets for the Strengthening of Concrete Columns after Elevated Temperatures: Experimental and Analytical Investigation

Effect of Textile Layers and Hydroxypropyl Methylcellulose on Flexural Behavior of TRLC Thin Plates

Study on model of flexure response of Carbon Fiber Textile Reinforced Concrete (CTRC) Sheets with short AR-glass fibers

Tensile Behavior of Basalt Textile Reinforced Concrete: Effect of Test Setups and Textile Ratios

Residual Flexural Behaviour of RC Beams Strengthened with TRC after ISO 834 Exposure

Investigation on the Flexural Behavior of Concrete Members Reinforced with Epoxy Resin-Impregnated Textiles

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Effects of temperature and strain rate on impact compression behaviors of three-dimensional carbon fiber/epoxy braided composites

Mechanical behaviour of TRC thin-plates exposed to high temperature: experimental study

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

High temperature mechanical performance and micro interfacial adhesive failure of textile reinforced concrete thin-plate

Flexural behavior of warp knitted textile reinforced concrete impregnated with cementitious binder

Bond Investigation Of Hybrid Textile With Self-Compacting Fine-Grain Concrete

Experimental study on mechanical properties of Textile Reinforced Concrete (TRC)

Mechanical behavior of textile reinforced concrete with newly developed mineral-impregnated carbon fabrics submitted to elevated temperatures

Experimental study on reinforced concrete beams strengthened with Basalt and Carbon Textile Reinforced mortars at elevated temperatures