Abstract:Fe-Ga alloys (Galfenol) are known to exhibit an unusually large magneto- striction, of order 320 ppm, which is attributed to the presence of nanoscale tetragonal Ga-rich $\mathrm {L}6 _{0}$ inclusions embedded in the bcc A2 Fe-rich matrix solid solution. The tetragonal axis in a particular nanoinclusion is determined by the orientation of nearest-neighbour Ga-Ga pairs. The distribution of these axes parallel to the three {100}directions means that the maximum magnetostriction can be achieved in a single crystal when the magnetic field is applied parallel to any cube edge. More recently it has been shown that traces of rare-earth atoms, $\approx 0.1$ at. %, which can be incorporated into these alloys when they are rapidly cooled, can greatly increase the magnetostric- tion by a factor of 2 – 3 [1]–[3]. The mode of action of the trace dopants has yet to be determined. Here we employ Mössbauer spectroscopy in an attempt to gain some insight into the location and mode of action of the trace rare earth dopants. The samples were produced by melt spinning. Precursor ingots of Fe 83 Ga 17 M x , with $\mathrm {M}=$ La, Nd, Sm, Tb and Tm and $x =0$, 0.05 or 0.25 were first prepared from 4N pure Fe and Ga by arc melting under argon four times and annealed at $1000 ^{o}\mathrm {C}$ in Ar to ensure homogeneity. The ingots were then melt spun on a copper wheel with a surface velocity of 20 ms $^{-1}$, to obtain ribbons about $50 \mu \mathrm {m}$ thick, and 5 mm wide. Transverse magnetostriction was measured by the strain gauge method in the direction of the ribbon length, with the field applied perpendicular to the plane of the ribbon. A field of up to 2 T was used to saturate the magnetization. Mössbauer spectra were obtained at room temperature in a conventional constant acceleration spec- trometer with a source of 57 Co in Rh. The spectrum of undoped Fe 83 Ga 17 is shown in Figure 1, together with associated fit to six hyperfine components [3]. It is composed of two main broad overlapping components with hyper- fine fields of 31.2 and 26.9 T, associated with iron in the A2 phase with 0 or 1 Ga neighbours [3]–[5]. They constitute 87 % of the total spectral area, and their ratio is 66:34, compared to a ratio 37:63 expected for a purely random distribution of Ga in the bcc phase. The Ga concentration in A2 on this basis should be 4.8 %, and the remainder is therefore Ga-rich. We identify two minor components with the tetragonal nanoinclusions, which make up 4.8 % of the total volume. One typical example of a doped sample, with 0.5 % La is shown in Figure 2. The sum of the spectra of iron with 0 and I Ga neighbours again represents 87 % of the total area, but the ratio to rises to 68:32, and the amount of iron in the tetragonal nanoinclusions rises to 5.6 % of the total. These are small changes, but they are observed systematically in spectra with five different rare earth dopants. We can therefore conclude that the rare earths serve to increase the volume of nanoinclusions in the sample, and they increase the amount of Ga present in the nanoinclusions. A second conclu- sion from the data is that there is no significant difference between the 0.05 % and 0.25 % doping, when they are measured for the same dopant. This shows that the solubility limit for the rare earth in these melt-spun ribbons is below 0.05 %. The conclusions are consistent with electron microscopy observations. We consider that the rare-earth dopant is probably initially incorporated into the nanoinclusions and it enhances their tetragonality up to the metastable solubility limit, which is less than 0.05 %. Beyond that, there is no further effect and the rare earth probably precipitates out in a 2:17 or 1:2 phase. In this way we can understand the strong influence of very small amounts of rare earth doping on the magnetostriction of Fe 83 Ga 17 .

Interaction of Trace Rare‐Earth Dopants and Nanoheterogeneities Induces Giant Magnetostriction in Fe‐Ga Alloys

Giant Heterogeneous Magnetostriction in Fe–Ga Alloys: Effect of Trace Element Doping

Understanding the Intrinsic Mechanism of the Giant Magnetostriction in Binary and Alloyed FeGa Solid Solutions

Mössbauer Investigation of Magnetostrictive Fe83Ga17 with Trace Rare- Earth Doping

The origin of large magnetostrictive properties of rare earth doped Fe-Ga as-cast alloys

Nanoheterogeneity response in large-magnetostriction Fe-Ga alloys: An in-situ magnetic small-angle neutron scattering study

Giant Magnetostriction in Nanoheterogeneous Fe-Al Alloys

Rare Earth Metals and Magnetostriction

Structural Origin For The Local Strong Anisotropy In Melt-Spun Fe-Ga-Tb: Tetragonal Nanoparticles

Local Inhomogeneous Structural Origin of Giant Magnetostriction in Fe-Ga Alloys

Tuning Magnetostriction of Fe–Ga Alloys Via Stress Engineering

Giant heterogeneous magnetostriction induced by charge accumulation-mediated nanoinclusion formation in dual-phase nanostructured systems

Large and sensitive magnetostriction in ferromagnetic composites with nanodispersive precipitates

Multiscale Influence of Trace Tb Addition on the Magnetostriction and Ductility of 〈100〉 Oriented Directionally Solidified Fe-Ga Crystals

Evolution of nanoheterogeneities and correlative influence on magnetostriction in FeGa-based magnetostrictive alloys

Giant enhancement of magnetostriction in Pt doped FeGa ribbons

Understanding Strong Magnetostriction in Fe100−xGax Alloys

Local Displacive Phase Transformation in Large-Magnetostriction Alloy Fe81Ga19

Giant magnetostriction in Tb-doped Fe83Ga17 melt-spun ribbons

Enhancing magnetostriction in FeAl alloys via crystal growth orientation tuning by a trace amount of Pt doping

Enhanced Magnetostriction of 〈001〉 Oriented Fe81Ga19 by Non-Rare-earth Element Doping