Large and sensitive magnetostriction in ferromagnetic composites with nanodispersive precipitates

Junming Gou,Tianyu Ma,Xiaolian Liu,Changsheng Zhang,Liangwei Sun,Guangai Sun,Weixing Xia,Xiaobing Ren
DOI: https://doi.org/10.1038/s41427-020-00276-7
IF: 10.761
2021-01-15
NPG Asia Materials
Abstract:Abstract Large and sensitive magnetostriction (large strain induced by small magnetic fields) is highly desired for applications of magnetostrictive materials. However, it is difficult to simultaneously improve magnetostriction and reduce the switching field because magnetostriction and the switching field are both proportional to the magnetocrystalline anisotropy. To solve this fundamental challenge, we report that introducing tetragonal nanoprecipitates into a cubic matrix can facilitate large and sensitive magnetostriction even in random polycrystals. As exhibited in a proof-of-principle reference, Fe–Ga alloys, the figure of merit—defined by the saturation magnetostriction over the magnetocrystalline anisotropy constant—can be enhanced by over 5-fold through optimum aging of the solution-treated precursor. On the one hand, the aging-induced nanodispersive face-centered tetragonal (FCT) precipitates create local tetragonal distortion of the body-centered cubic (BCC) matrix, substantially enhancing the saturation magnetostriction to be comparable to that of single crystal materials. On the other hand, these precipitates randomly couple with the matrix at the nanoscale, resulting in the collapse of net magnetocrystalline anisotropy. Our findings not only provide a simple and feasible approach to enhance the magnetostriction performance of random polycrystalline ferromagnets but also provide important insights toward understanding the mechanism of heterogeneous magnetostriction.
materials science, multidisciplinary
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to simultaneously achieve large magnetostriction and a low switching field in ferromagnetic materials. Generally, these two performance indicators are mutually contradictory because they are both directly proportional to magnetocrystalline anisotropy (MCA). Specifically, the better the magnetostriction performance of a material, the larger its switching field tends to be, which limits the performance of the material in practical applications, especially in applications requiring high sensitivity. To overcome this challenge, the author proposes a method of introducing tetragonal nano - precipitates in a cubic matrix to promote large and sensitive magnetostriction in random polycrystals. This method can not only significantly improve the magnetostriction performance of the material but also reduce its switching field, thereby improving the comprehensive performance of the material. ### Core problems of the paper 1. **How to simultaneously achieve large magnetostriction and a low switching field in ferromagnetic materials?** - The research found that in Fe - Ga alloys, through short - time isothermal aging treatment, dispersed face - centered tetragonal (FCT) nano - precipitates can be formed in the cubic matrix. These nano - precipitates can significantly improve the magnetostriction performance of the material, and due to the random coupling between the nano - precipitates and the matrix, the net magnetocrystalline anisotropy collapses, thereby reducing the switching field. 2. **Why can't the traditional single - crystal preparation method simultaneously achieve large magnetostriction and a low switching field?** - Although the traditional single - crystal preparation method can achieve relatively high magnetostriction performance, it is usually accompanied by a large switching field because the pre - stress and magnetic annealing in the single - crystal preparation process will introduce additional anisotropy. Therefore, a new method needs to be found to simultaneously optimize these two performance indicators. 3. **What is the specific influence of nano - precipitates on the magnetostriction performance?** - Through TEM characterization and SANS measurement, the research found that the L60 - type tetragonal nano - precipitates form local tetragonal distortion in the matrix. This distortion increases the spontaneous magnetostriction constant of the matrix, thereby improving the overall magnetostriction performance. At the same time, the random coupling between these nano - precipitates and the matrix leads to the collapse of the net magnetocrystalline anisotropy and reduces the switching field. ### Experimental results - **Improvement of magnetostriction performance**: After the optimal aging treatment, the saturation magnetostriction (λ//s) of the Fe - Ga alloy increases from the initial 50 - 65 ppm to 202 ppm, approaching the performance of single - crystal materials. - **Reduction of the switching field**: Through the aging treatment, the magnetocrystalline anisotropy constant (K1) is significantly reduced, which reduces the switching field of the material and improves the sensitivity of the material. - **Microstructural changes**: TEM characterization shows that after short - time aging treatment, L60 - type nano - precipitates with a size of about 20 nm are formed in the matrix. These precipitates are evenly distributed in the matrix and form local tetragonal distortion. ### Conclusion This research provides a simple and feasible method. By introducing tetragonal nano - precipitates in the cubic matrix, the goal of simultaneously improving the magnetostriction performance and reducing the switching field in random polycrystalline ferromagnetic materials is achieved. This finding not only provides new ideas for the development of high - performance magnetostriction materials but also provides important insights for understanding the heterogeneous magnetostriction mechanism.