Abstract:Zinc carbonate hydroxide nanobelts are prepared by the hydrolysis of zinc acetate aqueous solution in the presence of urea at 90 °C. The zinc carbonate hydroxide nanobelts can be facilely self-assembled in a circular flexible freestanding film with a diameter of 8.4 cm and thickness of ~48 μm. The calcination of the zinc carbonate hydroxide nanobelts at 300 °C under normal atmospheric condition results in the formation of ZnO nanowires. The zinc carbonate hydroxide nanobelts and resultant ZnO nanowires are characterized by XRD, SEM, TEM, TG-DSC, PL, and impedance measurement. The characterization results indicate that the ZnO nanowires exhibit unique nanostructure characterized by long chains of closely attached ZnO nanocrystals with ZnO/ZnO nanocrystal junctions. The unique ZnO nanowire-based UV photodetector exhibit much higher photoresponse currents (at the milliampere level) and on/off current ratio (~1000) than ZnO nanocrystal-based UV photodetector. Under the UV irradiance of 120 mW cm(-2) and low applied voltage of 0.5 V, the peak photoresponse current and on/off current ratio of the ZnO nanowire photodetector are 56 and 36 times higher than those of the ZnO nanocrystal UV photodetector, respectively. The reason for the superior photodetection performance of the ZnO nanowires over the ZnO nanocrystals is discussed.

Simple Fabrication ZnO/β-Ga2O3 Core/shell Nanorod Arrays and Their Photoresponse Properties

Performance Improvement of Ultraviolet Sensor of ZnO Nanorod Arrays

Non-aligned ZnO Nanowires Composited with Reduced Graphene Oxide and Single-Walled Carbon Nanotubes for Highly Responsive UV–visible Photodetectors

Dual-ultraviolet wavelength photodetector based on facile method fabrication of ZnO/ZnMgO core/shell nanorod arrays

Synthesis and photoresponse study of vertically oriented CuO/ZnO nanorod arrays based on solution methods

Honeycomb-like NiO/ZnO Heterostructured Nanorods: Photochemical Synthesis, Characterization, and Enhanced UV Detection Performance

Optical Properties of ZnO Nanorod-Based Heterogeneous Core/Shell Arrays

Fabrication and Performance of UV Photodetector of ZnO Nanorods Decorated with Al Nanoparticles

Highly sensitive ultraviolet photodetectors based on ZnO/SnO2 core-shell nanorod arrays

Preparation and Photodetection Property of ZnO Nanorods/ZnCo2O4 Nanoplates Heterojunction

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Controllable Growth of ZnO Nanorod Arrays on NiO Nanowires and Their High UV Photoresponse Current

A Hierarchical Structure Consisting of In2S3 Nanoparticles and ZnO Nanoarrays for UV Detection

Flexible and Transparent Ultraviolet Photodetector Enabled by Metal Doping ZnO Nanorods Based on Mica Substrate

β-Ga2O3 nanorod arrays with high light-to-electron conversion for solar-blind deep ultraviolet photodetection

ZnO@NiO Core-Shell Heterojunction Photoanode Modified with NiOOH Co-Catalyst for High-Performance Self-Powered Photoelectrochemical-Type UV Photodetector

Enhanced UV detection performance using a Cu-doped ZnO nanorod array film

High-performance UV photodetection of unique ZnO nanowires from zinc carbonate hydroxide nanobelts.

UV-photodetector Based on Heterostructured ZnO/(Ga,Ag)-co-doped ZnO Nanorods by Cost-Effective Two-Step Process

Enhanced ultraviolet photodetection with Ag nanoparticle-decorated ZnO nanowires and core-shell electrodes

Extended photo-response of ZnO/CdS core/shell nanorods fabricated by hydrothermal reaction and pulsed laser deposition.