Identification of Nano-Sized Precipitates in CLAM Steel Induced by 3.5 MeV Fe13+13+ion Irradiation
Ya Jing Guo,Yin Zhong Shen
DOI: https://doi.org/10.1016/j.jnucmat.2024.155307
IF: 3.555
2024-01-01
Journal of Nuclear Materials
Abstract:Nano-sized precipitate phases in normalized-and-tempered CLAM steel (HEAT-0912) before and after 3.5 MeV Fe 13+ ion irradiation at 400 degrees C to 0.61, 1.29 and 2.77 dpa were studied using transmission electron microscope and high-resolution transmission electron microscope. Six types of nanoprecipitate phases based on Cr23C6, 23 C 6 , TaC, Ta3C2, 3 C 2 , VC, Cr7C3, 7 C 3 , and V2C 2 C were identified in unirradiated steel. During irradiation, a large number of nano precipitates uniformly distributed in the matrix occurred, and the number density of nanoprecipitates initially increased and subsequently decreased with increasing the irradiation dose. Nanoscale Cr-rich M23C6, 23 C 6 , V-rich MX and M2X 2 X phases but no nanoscale phases based on TaC, Ta3C2 3 C 2 and Cr7C3 7 C 3 were identified in the steel irradiated up to 2.77 dpa. After irradiation, five types of irradiation-induced nanoscale new phases were identified in the irradiated steel. These include Fe-rich M3X2 3 X 2 (Cr3C2 3 C 2 types I and II) carbonitrides with the same simple orthorhombic lattice and totally different lattice parameters (approximately a/b/c = 1.146/0.552/0.2821 nm and 0.285/0.925/0.696 nm), Fe-rich M2C, 2 C, M3C 3 C and M5C2 5 C 2 carbides, but the occurrence of which under irradiation varied with the irradiation dose. Fe-rich M3X2 3 X 2 (Cr3C2 3 C 2 type I) and Fe-rich M5C2 5 C 2 phases were identified in the steel irradiated up to 1.29 dpa and only to 2.77 dpa, respectively. Fe-rich M2C 2 C and M3C 3 C in addition to Fe-rich M3X2 3 X (Cr3C2 3 C 2 type II) phases were identified in the steel irradiated up to 2.77 dpa. The irradiation-induced Fe-rich M3X2 3 X (Cr3C2 3 C 2 type I & II), M5C2 5 C 2 and M2C 2 C precipitates appear to be identified, for the first time, in reduced activation ferritic/martensitic steels including CLAM steel. The formation mechanism of these irradiation-induced precipitate phases is also discussed.