Identification of irradiation-induced phases in thermomechanically strengthened P92 steel after Fe ion irradiation at 700°C

Jiazheng Wang,Yinzhong Shen

DOI: https://doi.org/10.1016/j.jnucmat.2024.154960

IF: 3.555

2024-02-09

Journal of Nuclear Materials

Abstract:In order to study the changes of precipitate phases in TMT-strengthened high-chromium ferritic/martensitic steels under high-temperature irradiation conditions, TMT-strengthened P92 steel was irradiated with 3.5 MeV Fe 13+ ions at 700°C up to 0.74 dpa, and precipitate phases in the steel before and after irradiation were observed and analyzed using transmission electron microscopy and energy dispersive spectroscopy. As dominant phases in the steel, Nb-rich MX carbonitride, Cr-rich M 23 C 6 carbide and Cr-rich M 2 X carbonitride were still present in the steel after the irradiation. Irradiation-induced formation of six new precipitate phases occurred in the steel during the irradiation. Two irradiation-induced Cr-rich precipitates were identified as Cr-rich M 3 C 2 carbides with the same simple orthorhombic crystal structure and completely different lattice parameters. Three irradiation-induced Fe-rich precipitates were determined to be Fe-rich M 3 C carbide with a simple orthorhombic crystal structure, and two Fe-rich M 2 C carbides with the same simple orthorhombic crystal structure and completely different lattice parameters. Irradiation-induced Laves phase (Fe 2 Nb type) with a hexagonal crystal structure was also identified in the irradiated steel. These irradiation-induced phases are discussed.

materials science, multidisciplinary,nuclear science & technology

What problem does this paper attempt to address?

This paper aims to study the changes in precipitates in thermomechanically treated (TMT) high-chromium ferritic/martensitic steel (P92 steel) under high-temperature irradiation conditions. Specifically, the study involves irradiating P92 steel with 3.5 MeV Fe13+ ions at 700°C to a dose of 0.74 dpa, and observing and analyzing the precipitates in the steel before and after irradiation using transmission electron microscopy (TEM) and energy-dispersive X-ray spectroscopy (EDX).

The study found that under high-temperature irradiation conditions, the originally present niobium-rich MX carbonitrides, chromium-rich M23C6 carbides, and chromium-rich M2X carbonitrides in P92 steel still exist. Additionally, six new irradiation-induced precipitates were formed:
1. Two chromium-rich M3C2 carbides.
2. One iron-rich M3C carbide.
3. Two iron-rich M2C carbides.
4. One Laves phase (Fe2Nb type).

The specific structures and characteristics of these new phases are discussed in detail in the paper. Through this study, the authors hope to further understand the performance changes of thermomechanically treated high-chromium ferritic/martensitic steel under high-temperature irradiation conditions, thereby improving its application in fourth-generation nuclear reactors.