Crystal Structure, Microstructure, Thermal Expansion and Electrical Conductivity of CeO2–ZrO2 Solid Solution

Xiangnan Wang,Tao Liu,Cheng Wang,Jingkun Yu,Lin Li

DOI: https://doi.org/10.1080/17436753.2017.1358503

2017-01-01

Advances in Applied Ceramics

Abstract:CeO2-ZrO2 solid solution was synthesised by mechanical activation solid-state chemical reaction method and characterised by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal dilatometer, Hebb-Wagner method and DC van der Pauw method. The effects of CeO2 content on the crystal structure, microstructure, thermal expansion coefficient (TEC), electronic conductivity and total conductivity were investigated. XRD analysis showed that (25 and 75mol-%) CeO2-ZrO2 solid solutions corresponded to tetragonal and cubic phase, and 50mol-% CeO2-ZrO2 belonged to the mixture of tetragonal and cubic phases. SEM analysis showed that doping CeO2 was helpful to the sinterability of CeO2-ZrO2 samples. The TECs increased from 13.27x10(-6) to 14.72x10(-6)K(-1) with increasing CeO2 content. The electronic and total conductivities of 75mol-% CeO2-ZrO2 were largest, reaching 1.02x10(-4)Scm(-1) and 1.02x10(-2)Scm(-1) at 850 degrees C, respectively.