Abstract:As the traditional graphite-based composites cannot meet the requirement of rapid developing modern industry, novel sliding electrical contact materials with high self-lubricating performance in multiple environments are eagerly required. Herein a copper-based composite with WS2 and graphite as solid lubricant are fabricated by powder metallurgy hot-pressed method. The friction and wear behaviors of the composites with and without current are investigated under the condition with sliding velocity of 10 m/s and normal load of 2.5N/cm 2 in both air and vacuum. Morphologies of the worn surfaces are observed by optical microscope and compositions of the lubricating films are analyzed by XPS. Surface profile curves and roughness of the worn surfaces are obtained by 2205 surface profiler. The results of wear tests show that the friction coefficient and wear volume loss of the composites with current are greater than that without current in both air and vacuum due to the adverse effects of electrical current which damaged the lubricating film partially and roughed the worn surfaces. XPS results demonstrate that the lubricating film formed in air is composed of oxides of Cu, WS2 , elemental S and graphite, while the lubricating film formed in vacuum is composed of Cu, WS2 and graphite. Because of the synergetic lubricating action of oxides of Cu, WS2 and graphite, the composites show low friction coefficient and wear volume loss in air condition. Owing to the fact that graphite loses its lubricity which makes WS2 become the only lubricant, severe adhesive and abrasive wear occur and result in a high value of wear rate in vacuum condition. The formation of the lubricating film on the contact interface between the brush and ring is one of the factors which can greatly affect the wear performance of the brushes. The low contact voltage drop of the composites in vacuum condition is attributed to the high content of Cu in the surface film. This study fabricated a kind of new sliding electrical contact self-lubricating composite with dual-lubricant which can work well in both air and vacuum environments and provides a comprehensive analysis on the lubrication mechanisms of the composite.

Comparative Investigation into the Friction and Wear Behaviours of a Cu–Ag Contact Wire/carbon Strip and a Pure Copper Contact Wire/carbon Strip at High Speeds

Study on material transfer in the process of contact strips rubbing against a contact wire with electric current

Effect of the Vibration on Friction and Wear Behavior Between the Carbon Strip and Copper Contact Wire Pair

Experimental research on the friction and wear properties of a contact strip of a pantograph–catenary system at the sliding speed of 350km/h with electric current

Experimental Study on the Temperature of the Contact Strip in Sliding Electric Contact

A Comparative Investigation of the Tribological Behavior and Wear Mechanism of Bronze-graphite Composite under Dry- and Water-lubricated Sliding Against Steel

Research of Friction and Wear Behavior of Sliding Contacts under Strong Current Conditions

Research on the wear properties of carbon strips and contact wires at frigid temperatures

Correlation Between the Wear and Vibration of the Contact Strip in A Contact Wire Rubbing Against A Contact Strip with Electrical Current

The Study of Arc Rate, Friction, and Wear Performance of C/C Composites in Pantograph–Catenary System

Effect of Electrical Current Density, Apparent Contact Pressure, and Sliding Velocity on the Electrical Sliding Wear Behavior of Cu–Ti3AlC2 Composites

Friction and Wear Behavior of Copper-Graphite Composite Material in High-Speed Sliding with Current

Electrical Sliding Friction and Wear Properties of Cu–MoS2–graphite–WS2 Nanotubes Composites in Air and Vacuum Conditions

High-speed Electrical Sliding Wear Behaviors of Cu-WS2-graphite-WS2 Nanotubes Composite

Tribology performance of Cu-C/C composites with and without current

Study on the electrotribological property of Cu-Ag-Cr alloy

Study on Current-Carrying Tribological Characteristics of C-Cu Sliding Electric Contacts under Different Water Content

Comparative study of the current-carrying tribological properties of carbon graphite composites with different hardnesses

A comparative study on the electrical contact behavior of CuZn40 and AgCu10 alloys under fretting wear: Effect of current load

Effect of Electrical Current on the Tribological Behavior of the Cu-WS 2 -G Composites in Air and Vacuum

Study of the Friction and Wear of Electrified Copper Against Copper Alloy under Dry or Moist Conditions