Abstract:During the train operation, the pantograph/catenary system is subjected to an extremely harsh service environment. Relative humidity has a great influence on the current-carrying tribological behaviors of carbon strips. The identification and understanding of the wear mechanism are extremely important in wet and dry conditions. This study was carried out to investigate the humidity effect on the service properties of carbon sample rubbing against copper (Cu) with and without electric current using a home-made wear tester, and the humidity ranging from 10% RH to 80% RH. The results indicate that the sliding wear behavior of the friction interface is drastically affected by the intervention of water vapor and electric current. The coefficient of friction (COF) without current is obviously lower than current-carrying sliding when the humidity is constant. However, the increased humidity led to a decreasing trend. After the current increases to 10 A, all the COF values are closed to each other ultimately. These phenomena mainly result from the formation and destruction of water lubrication film. Furthermore, the tribo-pairs worn surface appears the most sensitive to the current effect under dry conditions. The reverse transfer of Cu and carbon is greater on account of the current agglomeration effect, and the oxidation degree is more severe. The wear mechanisms of carbon are mainly material transfer accompanying with oxidation erosion. However, the wear degradation is weakened under water lubrication and uniform current distribution which improves the conductive quality. This is the coupling effect of humidity environment, current and heat concentration. This experiment provides technical support for the operation of an electric locomotive under an extremely harsh service environment.

Influence of electric current on the temperature rise and wear mechanism of copper-graphite current-carrying friction pair

Friction and Wear Behavior of Copper-Graphite Composite Material in High-Speed Sliding with Current

Effect of Electrical Current on the Tribological Property of Cu-Graphite Brush

Research of Friction and Wear Behavior of Sliding Contacts under Strong Current Conditions

Study the influence of power-current impact with different conditions on the current-carrying wear property of carbon brush/friction disc contact

Tribology performance of Cu-C/C composites with and without current

The role of relatively humidity in friction and wear behaviors of carbon sliding against copper with electric current

Effect of the Vibration on Friction and Wear Behavior Between the Carbon Strip and Copper Contact Wire Pair

Research on Frictional Wear Properties of C/C Composite with Electric Current

Comparative Investigation into the Friction and Wear Behaviours of a Cu–Ag Contact Wire/carbon Strip and a Pure Copper Contact Wire/carbon Strip at High Speeds

Tribological and Conductive Behavior of Cu/Cu Rolling Current-Carrying Pairs in a Water Environment

Study on Current-Carrying Tribological Characteristics of C-Cu Sliding Electric Contacts under Different Water Content

Study on the Damage Mechanism of an H62-Cu/7075-Al Tribo-Pair Under the Influences of Current Direction and Density

Progress on Current-Carry Friction and Wear: An Overview from Measurements to Mechanism

Study of the Friction and Wear of Electrified Copper Against Copper Alloy under Dry or Moist Conditions

Effect of Current Density on Surface Temperature and Tribology Behavior of Chromium Bronze/brass Couple

Research Progress on Current-Carrying Friction with High Stability and Excellent Tribological Behavior

Comparative study of the current-carrying tribological properties of carbon graphite composites with different hardnesses

Effect of current on the tribological behavior of Cu-Fe-P immiscible alloy produced by laser powder bed fusion

Capacity Evaluation on Cu Rolling Tribological/electric Contact Pairs under Various Contact Load and Applied Voltage

The Influence of Temperature and Load on Dry Sliding Wear and Friction Property of Low Metallic Friction Material