Influences of Element Segregation on the Magnetic Properties in Nanocrystalline Nd-Ce-Fe-B Alloys
Lizhong Zhao,Chengli Li,Zhipeng Hao,Xiaolian Li,Xuefeng Liao,Jiasheng Zhang,Kunpeng Su,Lingwei Li,Hongya Yu,Jean-Marc Greneche,Jiaying Jin,Zhongwu Liu
DOI: https://doi.org/10.1016/j.matchar.2018.12.022
IF: 4.537
2019-01-01
Materials Characterization
Abstract:The RE-rich (Ce1-xNdx)(16)Fe78B6 (x = 0-1) nanocrystalline alloys were prepared by melt-spinning method. The transmission electron microscopy equipped with EDS was employed to investigate the microstructure and rare-earth element segregation. The average Nd/RE ratios in 2:14:1 grains are 22, 52, 67, 74, 78, and 81% for the x = 0.1, 0.4, 0.5, 0.6, 0.7, and 0.8 alloys, respectively, which are larger than the nominal ratios, indicating a Nd segregation in 2:14:1 phase. The Nd/RE ratio changing with x shows a two-stage of increment: the average increment in x = 0.1-0.5 alloys is much higher than that of x = 0.5-0.8 alloys. The corresponding change is also observed in the plotted intrinsic parameters of cell volume V, hyperfine field B-hf, and spin reorientation temperature T-SR of the 2:14:1 phase changing with x curves. The high Ce-contained RE-rich Nd-Ce-Fe-B with strong element segregation shows high coercivities and high performance/price ratio. The present results thus contribute to understanding the fundamental mechanism of Ce-contained Nd-Ce-Fe-B permanent magnets and taking advantage of the element segregation.