Solidification Microstructure Evolution and Mechanical Properties of Casting Ti-48Al-2Cr-2Nb-(Ni,TiB2)Alloy
Wang Hao,Xie Guangming,Jia Yi,Yao Haoming,Xiao Shulong,Chen Yuyong,Han Jianchao,Wang Tao
2022-01-01
Rare Metal Materials and Engineering
Abstract:With excellent specific strength, specific modulus and service performance at high temperature, TiAl-based alloys have become the key material for the update of aerospace engineering. However, the coarse as-cast grain size, low room temperature plasticity and strength limit their further engineering application. In this paper, the Ti-48Al-2Cr-2Nb ingot alloyed with TiB2 and Ni was prepared by the induction melting, and the effects of TiB2 and Ni on the solidification microstructure and mechanical properties were studied. The results show that the addition of TiB2 and Ni exhibits little influence on the solidification path and primary phase. The grain size is refined from 700 mu m to 100 mu m, and the flake TiB2 and Ni-riched tau(3) phase is determined. The nanohardness of tau(3) phase is detected as 8.3 GPa, which is significantly higher than that of lamellar colony and bulk gamma phase. Tensile strength of T4822-(Ni,TiB2) alloy is similar to that of the matrix alloy, and the fracture elongation is increased by 30% at room temperature. At 700 similar to 900 degrees C, T4822-(Ni,TiB2) alloy shows the preferable tensile strength, and the tensile strength at 900. reaches 365 MPa, 9% higher than that of the matrix alloy. At 800 and 900 degrees C, the breaking elongation reaches 25.3% and 36.1%, respectively, much higher than that of the matrix alloy. The refinement of grain size and the massive gamma phase at grain boundary are the main reasons for the plasticity improvement of T4822-(Ni,TiB2) alloy. And the good high temperature strength can be attributed to the hard borides and Ni-rich tau(3) phase inside and at the interface of lamellar masses.