Study on the Deformation Behavior of Β Phase in Ti–10V–2Fe–3Al Alloy by Micro-Indentation

Xinkai Ma,Fuguo Li,Jun Cao,Zhankun Sun,Qiong Wan,Jinghui Li,Zhanwei Yuan
DOI: https://doi.org/10.1016/j.jallcom.2017.01.235
IF: 6.2
2017-01-01
Journal of Alloys and Compounds
Abstract:The Ti-10V-2Fe-3Al alloy composed of beta phases was varied by the beta-solution treatment. In order to characterize the indentation deformation behavior of b phase, the micro-indentation tests were conducted in the indenter load ranging from 50 mN to 450 mN and the loading rates range from 4.84 mN/s to 19.36 mN/s at ambient temperature. The influences of beta-solution treatment temperature, loading rate and indenter load on the micromechanics properties were investigated. The results showed that both the micro-hardness and Young's modulus of beta phase declined drastically with the increase of indenter load, while remained the same level when the indenter load was above 300 mN. It was observed that the specimen under beta-solution treatment of 820 degrees C and the loading rate of 19.36 mN/s possessed a higher micro-hardness and Young's modulus than that of others. The plastic energy dissipation, which was significantly influenced by the beta-solution treatment temperature and loading rate, increased with the growth of indenter load exerted on the specimens and can be expressed in a power-law function of indenter load for b phase. In addition, the average plastic energy dissipation density in the microindentation was a linear function of the micro-hardness and its decrease with indenter load is attributed to the decline of geometrically necessary dislocations (GNDs). (C) 2017 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?