Sustainable Acrylic Acid Making via Acetic Acid–Formaldehyde Condensation: The Highly Selective and Durable VPO-TiO 2 Catalyst Accomplished by VPO Phase Control and Wet Co-Mechanical Milling
Jun Liu,Pengcheng Wang,Peiwen Xu,Zhijia Xu,Xinzhen Feng,Weijie Ji,Hamidreza Arandiyan,Chak-Tong Au
DOI: https://doi.org/10.1021/acssuschemeng.0c05916
2020-11-25
Abstract:On the basis of the precise phase control of vanadium phosphorus oxides (VPOs), nanosized TiO<sub>2</sub> was employed as a dopant/dispersant to fabricate a series of VPO-TiO<sub>2</sub> catalysts through a wet mechanical co-milling process. The resulting catalysts showed outstanding durability plus excellent target products [acrylic acid (AA) + methyl acrylate (MA)] selectivity via acetic acid (HAc)–formaldehyde (FA) condensation. Over an optimized catalyst of 20% VPO-TiO<sub>2</sub>, the (AA + MA) selectivity being 85% (HAc input-based) at a yield level >60% (FA input-based) can be achieved after 180-h running, the best known to date over the VPO-based catalysts. The detailed characterizations including X-ray powder diffraction, Raman spectra, XPS, and H<sub>2</sub>-TPR indicated that the V<sup>5+</sup> in the original VOPO<sub>4</sub> phase would be partially reduced in the presence of TiO<sub>2</sub> after the milling process in the cyclohexane medium; and the partially reduced VOPO<sub>4</sub> phase together with the decorated TiO<sub>2</sub> component stabilized the remaining V<sup>5+</sup> entities and considerably slowed down the continuous reduction of surface V<sup>5+</sup> species, accounting for substantially enhanced catalyst durability as well as target product selectivity. The NH<sub>3</sub>-/CO<sub>2</sub>-TPD results demonstrated that the surface acid–base property also varied notably with the VPO content which in turn controlled the HAc conversion and (MA + AA) selectivity accordingly.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c05916?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c05916</a>.Detailed experimental procedures; H<sub>2</sub>-TPR profiles, XPS data, and NH<sub>3</sub>(CO<sub>2</sub>)-TPD profiles of the catalysts with different VPO loading; NH<sub>3</sub>(CO<sub>2</sub>)-TPD profiles, XRD patterns, Raman spectra, and XPS data of the catalysts fabricated different way of TiO<sub>2</sub> introduction; and NH<sub>3</sub>-TPD profiles and XPS data of the used and regenerated 20%VPO-TiO<sub>2</sub> catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c05916/suppl_file/sc0c05916_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology