Effect of neodymium on microstructure, mechanical properties, and corrosion behavior of Mg-2Si- x Nd alloys fabricated by powder metallurgy
Yudi Nugraha Thaha,Bintoro Siswayanti,Bunga Rani Elvira,Adi Noer Syahid,Nadia Rachmawati,Aprilia Erryani,Daniel Panghihutan Malau,Dhyah Annur,Franciska Pramuji Lestari,Talitha Asmaria,Muttaqin,Ika Kartika,Albertus Deny Heri Setyawan
DOI: https://doi.org/10.1016/j.jre.2024.11.011
IF: 4.632
2024-11-11
Journal of Rare Earths
Abstract:Highlights • The effect of Nd content of 0.05 wt%–0.20 wt% on the microstructure, compressive behavior, and corrosion resistance of Mg-2Si- x Nd powder metallurgy (PM) alloys was investigated. • Increasing Nd content refines the grain aspect ratio of Mg-2Si- x Nd PM alloys. • Increasing Nd content enhances the compressive strength, hardness and corrosion resistance of Mg-2Si- x Nd PM alloys. In the present work, the effects of neodymium (Nd) on microstructure, mechanical performance, and corrosion behavior of powder metallurgy Mg-2Si- x Nd ( x = 0.05 wt%, 0.15 wt%, and 0.20 wt%) alloys were investigated. Microstructures were examined by optical and scanning electron microscopes combined with an energy-dispersive spectrometer. Hardness and compressive tests were used to study the mechanical properties of alloys. Potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), Mott-Schottky analysis, and the hydrogen evolution test were applied to characterize the corrosion behavior of alloys in Hanks' solution. The microstructure of Mg-2Si- x Nd alloys mainly consists of α-Mg matrix, Mg 2 Si, and MgNd phases. The increase in Nd content tends to decrease the aspect ratio of α-Mg grains, which leads to the enhancement of the ultimate-compressive strengths and hardness of the alloys. Potentiodynamic polarization shows that increasing Nd content leads to a lower corrosion current density in the Mg-2Si- x Nd alloys. The EIS results confirm that a higher addition of Nd suppresses the dissolution kinetics of the alloys due to the increasing charge transfer resistance. Mott-Schottky analysis reveals the formation of an n-type semiconductive passive film on the alloy surfaces, where the interstitial and oxygen vacancies predominate over the metal vacancies. The X-ray photoelectron spectroscopy (XPS) reveals that a mixture of Mg(OH) 2 , MgO, MgCO 3 , and Nd 2 O 3 has formed as the corrosion products on the Mg-2Si- x Nd alloy surfaces after a longer immersion time in Hanks' solution. Graphical abstract Mg-2Si- x Nd alloys were fabricated by powder metallurgy (PM) method. Increasing Nd content ( x ) from 0.05 wt% to 0.20 wt% enhances the ultimate compression strength, hardness and corrosion resistance of Mg-2Si- x Nd PM alloys. Download: Download high-res image (273KB) Download: Download full-size image
chemistry, applied