Abstract:Due to the moderate degradation rates and acceptable biocompatibility, Zn-based alloys have attracted more and more attention as biodegradable materials. However, the inferior strength and ductility significantly limit their further applications. In this work, biodegradable Zn-2Cu-0.2Mn-xLi (x = 0, 0.1 and 0.38) alloys were developed with enhanced comprehensive mechanical properties. Also, these novel alloys were found to possess extraordinary antibacterial activity and good biocompatibility. Annealing and hot extrusion were performed on the as-cast alloys. The microstructures, mechanical properties, corrosion behavior, antibacterial ability, hemocompatibility and cytocompatibility of the alloys were systematically studied. Microstructure analysis indicates that primary e-CuZn4 particles are distributed in the Zn grains in all ascast alloys. Addition of Li leads to formation of beta-LiZn4 phase in eutectics and beta-LiZn4 precipitates within the Zn grains. In the as-annealed alloy, secondary epsilon-CuZn4 precipitates and fine beta-LiZn4 precipitates appear in the Zn matrix of the Li-containing alloys. All the as-extruded alloys reveal fibrous morphology and develop (0001) basal texture. Mechanical property test shows that all as-extruded alloys exhibit excellent strength and ductility which can fully meet the benchmark requirement for biodegradable materials. It is worth to notice that, Zn-2Cu-0.2Mn-0.38Li alloy has a tensile yield strength, ultimate tensile strength and elongation as high as 424 +/- 28.3 MPa, 445 +/- 11.1 MPa and 76 +/- 3.35%, respectively. The 24-day in vitro immersion test in the SBF solution shows that the corrosion rates were 0.212 +/- 0.007 mm/year for Zn-2Cu-0.2Mn, 0.197 +/- 0.005 mm/year for Zn-2Cu-0.2Mn-0.1Li and 0.184 +/- 0.008 mm/year for Zn-2Cu-0.2Mn-0.38Li, respectively. It indicates that addition of Li improves the corrosion resistance of the alloys. All as-extruded alloys have antibacterial rates of >= 99% and hemolysis rates of < 5%, exhibiting strong antibacterial activity and good hemocompatibility. The MC3T3-E1 cells show more than 95% viability in 25% extracts of all asextruded alloys in all culturing days. In addition, in this low concentration of extracts, the cells in the alloy groups exhibit good spreading morphology and high ALP expression, suggesting good cytocompatibility. (c) 2022 Elsevier B.V. All rights reserved.

Effects of Li on Microstructures, Mechanical, and Biocorrosion Properties of Biodegradable Mg94‐xZn2Y4Lix Alloys with Long Period Stacking Ordered Phase

Modification of Mn on Corrosion and Mechanical Behavior of Biodegradable Mg88Y4Zn2Li5 Alloy with Long-Period Stacking Ordered Structure

Effect of the Morphology of Long-Period Stacking Ordered Phase on Mechanical Properties and Corrosion Behavior of Cast Mg-Zn-Y-Ti Alloy

Effects of Li addition on the properties of biodegradable Zn–Fe–Li alloy: Microstructure, mechanical properties, corrosion behavior, and cytocompatibility

Effect of long period stacking ordered structure on the biocorrosion resistance and osteogenesis ability of Mg–Zn–Y-Mn alloys

Insight into Role and Mechanism of Li on the Key Aspects of Biodegradable ZnLi Alloys: Microstructure Evolution, Mechanical Properties, Corrosion Behavior and Cytotoxicity

Effect of Li on Formation of Long Period Stacking Ordered Phases and Mechanical Properties of Mg-Gd-Zn Alloy

Biocorrosion Behavior and Cytotoxicity of a Mg–Gd–Zn–Zr Alloy with Long Period Stacking Ordered Structure

Effects of Li on the Microstructure and Mechanical Properties of Long Period Stacking Ordered Mg94Zn4Y2 Alloy

Novel Zn-2Cu-0.2Mn-xLi (x = 0, 0.1 and 0.38) Alloys Developed for Potential Biodegradable Implant Applications

Study on the Mg-Li-Zn Ternary Alloy System with Improved Mechanical Properties, Good Degradation Performance and Different Responses to Cells.

Microstructures, Mechanical Properties and in Vitro Corrosion Behavior of Biodegradable Zn Alloys Microalloyed with Al, Mn, Cu, Ag and Li Elements

Effects of Li Addition on Microstructure and Mechanical Properties of Rapidly Solidified Mg96.5Gd2.5Zn1 Alloy

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Corrosion Behaviors of Long‐Period Stacking Ordered Structure in Mg Alloys Used in Biomaterials: A Review

High-performance Extruded Mg89Y4Zn2Li5 Alloy with Deformed LPSO Structures Plus Fine Dynamical Recrystallized Grains

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Investigation on Microstructures, Mechanical Properties and in Vitro Corrosion Behavior of Novel Biodegradable Zn-2Cu-0.01Ti-xLi Alloys

Investigation on the Microstructure, Mechanical Properties, in Vitro Degradation Behavior and Biocompatibility of Newly Developed Zn-0.8%Li-(Mg, Ag) Alloys for Guided Bone Regeneration.

In Vitro Degradation and Biocompatibility of Mg-Li-Ca Alloys—the Influence of Li Content

Microstructure characterization and corrosion behavior of Mg–Y–Zn alloys with different long period stacking ordered structures