Abstract:In this study, the creep crack growth （CCG） properties and fracture mechanism of a Cr-Mo-V steel at 566 C in compact tension （CT） specimens were investigated, and the CCG rate was predicted by using the NSW model. The results show that the CCG rate measured by CT specimens is much lower than that predicted by the NSW model under plane-strain state. This means that the NSW model prediction for the CCG rate of the steel is over-conservative. In addition, the CCG rate da/dt versus C measured by the experiments shows the piecewise linear relation on log-log scale instead of a single linear relation predicted by the NSW model. The main reasons for these results are that the actual creep fracture mechanism of the steel and the actual creep crack tip stress field in the CT specimens have not been fully captured in the NSW model. The experimental observation shows that the creep crack propagates in a discontinuous way （step by step） at meso-scale, and the cracks at micro-scale are usually formed by the growth and coalescence of voids on grain boundaries. The NSW model based on the creep ductility exhaustion approach may not correctly describe this creep fracture process. In addition, the opening stress and triaxial stress ahead of crack tips calculated by three-dimensional finite element method is lower than those predicted by the HRR stress field which is used in the NSW model under plane-strain state. The use of the high HRR stress field will cause high CCG rates. The change in the creep fracture mechanism at micro-scale in different ranges of C may cause the piecewise linear relation between the da/dt and C . Therefore, it is necessary to study the actual CCG mechanism in a wide range of C and the actual creep crack tip stress field to establish accurate CCG prediction models.

Prediction of creep crack initiation in Cr–Mo–V steel specimens with different geometries

Prediction of Creep Crack Initiation Time Based on Constraint Parameters in Specimens with Different Geometries

Numerical Prediction of Creep Crack Growth Rate in Cr-Mo-V Steel for Specimens with Different Constraints

Prediction of creep crack growth behavior in Cr–Mo–V steel specimens with different constraints for a wide range of C ∗

The influence of stress-regime dependent creep model and ductility in the prediction of creep crack growth rate in Cr–Mo–V steel

Effect of constraint on creep fracture toughness of a Cr-Mo-V steel

Creep Crack Growth in A Cr-Mo-V Type Steel: Experimental Observation and Prediction

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Prediction of Creep Crack Initiation Behavior Considering Constraint Effects for Cracked Pipes

Effect of the Out-Of-Plane Constraint on Creep Crack Growth Property of Cr-Mo-V Type Steel

Geometry and Material Constraint Effects on Creep Crack Growth Behavior in Welded Joints

A damage mechanics approach to the prediction of creep crack growth

Effect and Mechanism of Out-of-plane Constraint on Creep Crack Growth Behavior of a Cr–Mo–V Steel

Microstructural Damage Mechanics-Based Model for Creep Fracture of 9%cr Steel under Prior Fatigue Loading

Effect of stress dependent creep ductility on creep crack growth behaviour of steels for wide range of C*

Creep crack growth prediction using a damage based approach

Modelling short crack growth under creep-fatigue interaction for different dwell times

A Robust Life Prediction Model for a Range of Materials under Creep-Fatigue Interaction Loading Conditions

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

A More Appropriate FE Model to Predict the Creep Crack Initiation and Growth Behavior of Brazed Joint

Creep Crack Growth Behavior Analysis of the 9Cr-1Mo Steel by a Modified Creep-Damage Model