Effect of β recrystallization on the precipitation evolution of primary α phase and the phase transformation inheritance during thermomechanical processing in Ti-55511 alloy
Yue Dong,Xingang Liu,Haozhe Niu,Hao Xu,Yini He,Yujiao Ke,Wenwen Zhang
DOI: https://doi.org/10.1016/j.jmrt.2023.10.136
IF: 6.267
2023-10-30
Journal of Materials Research and Technology
Abstract:The crystallographic defects introduced after thermal deformation of near-β Ti-55511 alloy can have an important impact on the precipitation of primary α phase (α p ), β grain evolution and the texture evolution during the subsequent heat treatment. The investigation indicates that the intragranular short-rod α p precipitated by strain-induced nucleation deviates from Burgers orientation relationship (BOR) by boundary splitting in 0.27–0.64, accompanied by β→α p transformation, which strictly obeys BOR during ST. In addition, the strain and strain rate can modify the α p -type after deformation. Three main α p types are Type I: 50–60°/ , Type II: 40–50° or 80–90°/ and Type III: 90–100°/ . The phase transformation inheritance occurs after ST based on the variant selection effect, and the α p varieties are mainly 80–90°/ and 80–90°/ . Furthermore, the density of the deformation texture (000–1) [11–20] is weakened by the new α p transformation texture (0001) [-1-780] and the recrystallization texture (23-5-3) [11–22], but it is inherited at 1.23. However, the α p recrystallization texture significantly restrains the occurrence of the deformation texture inheritance phenomenon at 0.001 s −1 . Moreover, the adjacent α p grains are mainly 60°/ to each other, while the β grains around α p with a relatively high degree of recrystallization are mainly 30–50°/ to each other. The first one of the static sphericalized α p is partly generated by coarsening, which is derived from the dispersed nucleus α p precipitated at the trigonal/tetragonal β sub-boundaries. The second one is by the GB separation mechanism triggered by the formation of α/α boundaries within the short-bar α p grain.
materials science, multidisciplinary,metallurgy & metallurgical engineering