Multistage-aging Process Effect on Formation of GP Zones and Mechanical Properties in Al–Zn–Mg–Cu Alloy

Rong-xian Yang,Zhi-yi Liu,Pu-you Ying,Jun-lin Li,Liang-hua Lin,Su-min Zeng

DOI: https://doi.org/10.1016/s1003-6326(16)64221-8

2016-01-01

Abstract:The tensile properties and fatigue behavior of an Al?Zn?Mg?Cu alloy were investigated by performing tensile tests and fatigue crack propagation (FCP) tests. The tensile results show that lower aging temperature modified retrogression and re-aging (RRA) process enhances the elongation, but reduces the strength of the alloy, as compared to conventional RRA process which employs peak aging temperature. Both ductility and strength, however, are increased by employing a natural aging prior to re-aging based on the former modified RRA process. Fatigue test results show that both routes reduce FCP rate. Especially, the lower re-aging temperature modified RRA process obtains the lowest FCP rate. Natural aging treatment could enhance the nucleation rate of GP zones. A large amount of GP zones could be cut by dislocations, which is responsible for the highest tensile strength and elongation, as well as lower FCP rate.