Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Low Cycle Creep-Fatigue Behavior of Nickel Base Superalloy GH536

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

High-temperature low cycle fatigue behavior of nickel based superalloy GH536

Low Cycle Fatigue and Creep-Fatigue Interaction Behavior of Nickel-Base Superalloy GH4169 at Elevated Temperature of 650 °C

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Low-Cycle Fatigue-Creep Interaction Behavior of GH4169 Supperalloy

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

The Influence of Dwell Time on Low Cycle Fatigue Behavior of Ni-Base Superalloy Ic10

The creep-fatigue behavior of a nickel-based superalloy: Experiments study and cyclic plastic analysis

High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

Investigation on Microstructure Evolution and Fracture Morphology of Single Crystal Nickel-Base Superalloys under Creep-Fatigue Interaction Loading

Tensile and low cycle fatigue properties of nickel-base powder metallurgy superalloy FGH95

Cycle-dependent creep-fatigue deformation and life predictions in a nickel-based superalloy at elevated temperature

Creep-fatigue Behavior of Nickel-Based Single Crystal Superalloy with Different Orientations: Experimental Characterization and Multi-Scale Simulation

Low Cycle Fatigue Behavior and Life Evaluation of a P/M Nickel Base Superalloy under Different Dwell Conditions

Creep-fatigue Behavior of Nickel-based Superalloy GH720Li

Fatigue-creep Behaviors of Ni–Fe Based Superalloy under Various Testing Conditions

Influence of Notch on Creep Properties of GH3536 Nickel-Based Superalloy

Creep Residual Life Prediction of a Nickel-Based Single Crystal Superalloy Based on Microstructure Evolution

Multiaxial Fatigue Behavior of Ni-based Superalloy GH4169 at 650°C

Creep–fatigue Interaction Behavior of Nickel-Based Single Crystal Superalloy at High Temperature by In-Situ SEM Observation