CHANGE IN DENSITY OF Α-Fe DURING HEALING OF INTERNAL FATIGUE MICROCRACKS UNDER ANNEALING

HL Zhang,J Sun

DOI: https://doi.org/10.3321/j.issn:0412-1961.2003.04.004

IF: 1.797

2003-01-01

ACTA METALLURGICA SINICA

Abstract:The plastic-strain-controlled fatigues with uniaxial symmetric and tension-compression loadings at room temperature were performed on pure iron specimens. The as-fatigued specimens were then annealed in vacuum at 1173 K from 1 h to 7 h. The morphologies of internal cracks were observed by SEM upon the as-fatigued and as-annealed specimens, respectively. The change in the density of specimens was measured by the electronically analytical balance. The results show that, compared with the initial density, the density for the as-fatigued specimens becomes smaller as increasing the fractional fatigue life, and is nearly constant when the specimens were annealed from 1 h to 3 h, but increases gradually when annealed after 3 h, and approximates eventually to the initial density at the point of 7 h annealing. It indicates that the decrease in density of as-fatigued specimens is due to crack initiation within the specimens. At the early stage of annealing, the specimen density is nearly constant because the crack morphological change is controlled by surface diffusion; at the later stage, it increases and finally comes to the initial density because the voids evolved from the parent crack are reduced by volume diffusion coupled with grain boundary diffusion.