Abstract:A new process for recycling zinc and copper from the smelting slag of waste brass was investigated in this study. The zinc and copper present in the smelting slag were dissolved in a ZnCl2-NH4Cl solution system. To recycle copper, the lixivium was purified by a novel method termed as electrochemistry and chemistry synergetic (ECS) purification. After deep purification of the ECS-treated lixivium by zinc powder cementation, zinc in the lixivium was extracted by electrowinning to obtain a zinc plate. The effects of the leaching temperature, reaction time, and liquid-solid ratio on the extraction percentages of zinc and copper were examined. The results revealed that the extraction percentages of zinc and copper were 88.37% and 90.85%, respectively, at a leaching temperature of 95 degrees C, reaction time of 90 min, and liquid-solid ratio of 8:1 mL/g. Further, effects of the current density, temperature, and reaction time on the recovery ratio of copper by ECS method were examined. The results revealed that 98.51% of copper could be extracted from the lixivium and that the purity of the extracted copper was 96.7% at a temperature of 70 degrees C and cathode current density of 75 A/m(2) after a reaction for 4 h. In the deep purification process, 0.3 g/L zinc powder was used to completely remove impurities from the ECS-treated lixivium. In the zinc electrowinning process, a current efficiency of 95.79% was achieved at 70 degrees C and 400 A/m(2); the purity of the obtained zinc product was greater than 99.95%, and the direct energy consumption was 2966.59 kW.h/t-Zn.

Electrowinning Cu and Zn from a Strong Copper Cyanide Solution

RECOVERY OF Cu, Zn AND CYANIDE FROM STRONG COPPER CYANIDE SOLUTIONS BY ELFETROWINNING-PARTIAL ACIDIZING

Study on Electrowinning Sheet-form Copper from Acidic Etchant Waste in Diaphragm Cell

Hydrometallurgical Stepwise Recovery of Copper and Zinc from Smelting Slag of Waste Brass in Ammonium Chloride Solution

Study on Electrowinning Zinc in Zn(II)NH_3-NH_4Cl-H_2O System

Recovery of Copper and Nickel from Electroplating Sludge by Cyclone Electrowinning

Removal and Influence of Copper Ion on Lead Electrowining in Alkaline Solution

Effect of Zn2+ on the extraction of copper by cyclone electrowinning from simulated copper-containing electrolyte

Electrowinning zinc in the system of zn(II)-NH3-NH 4CI-H2Q and mechanism of anodic reaction

Leaching kinetics of copper and valuable metal extraction from copper-cadmium residues of zinc hydrometallurgy by oxidation acid leaching

Advances and Future Prospects for Copper Electrowinning

Preparation of High- Purity Zinc from Zinc Calcine by an Ammonia Process

Study on the Copper Sulfate Crystalline Mother Liquor by Eletrodialysis Process

Application of Copper for Sufficient Metal Extraction from Zinc Leaching Residue: Process Optimization and Copper Reuse

Advanced Treatment of Copper Smelting Wastewater by the Combination of Internal Micro-Electrolysis and Electrocoagulation

Recovery of Zinc from Low-Grade Zinc Oxide Ores by Solvent Extraction

The study of direct gold electrowinning from dilute cyanide solutions

A New Process for Recovering of Zinc From Blast Furnace Sludge(Ⅱ): Solvent Extraction and Electrowinning

Studies on Leaching of Oxidized Copper Ore from South America

A Novel Strategy Achieving Enrichment of Metal Values from and into Ammoniacal Solutions

Test Research on Separate of Iron and Recovery of Copper,Zinc From A Acidic Leaching Solution of Zinc Hydrometallurgy Slag