Abstract:The multiseeding technique is a method to grow large-sized REBa2Cu3O7−δ (REBCO, where RE is a rare earth element) high temperature superconducting bulks. However, due to the existence of grain boundaries between seed crystals, the superconducting properties of bulks are not always better than those of single grain bulks. In order to improve the superconducting properties caused by grain boundaries, we introduced buffer layers with a diameter of 6 mm in the growth of GdBCO bulks. Using the modified top-seeded melt texture growth method (TSMG), that is, YBa2Cu3O7−δ (Y123) as the liquid phase source, two GdBCO superconducting bulks with buffer layers with a diameter of 25 mm and a thickness of 12 mm were successfully prepared. The seed crystal arrangement of two GdBCO bulks with a distance of 12 mm were (100/100) and (110/110), respectively. The trapped field of the GdBCO superconductor bulks exhibited two peaks. The maximum peaks of superconductor bulk SA (100/100) were 0.30 T and 0.23 T, and the maximum peaks of superconductor bulk SB (110/110) were 0.35 T and 0.29 T. The critical transition temperature remained between 94 K and 96 K, with superior superconducting properties. The maximum JC, self-field of SA appeared in specimen b5, which was 4.5 × 104 A/cm2. Compared with SA, the JC value of SB had obvious advantages in a low magnetic field, medium magnetic field and high magnetic field. The maximum JC, self-field value appeared in specimen b2, which was 4.65 × 104 A/cm2. At the same time, it showed an obvious second peak effect, which was attributed to Gd/Ba substitution. Liquid phase source Y123 increased the concentration of the Gd solute dissolved from Gd211 particles, reduced the size of Gd211 particles and optimized JC. For SA and SB under the joint action of the buffer and the Y123 liquid source, except for the contribution of Gd211 particles to be the magnetic flux pinning center with the improvement of JC, the pores also played a positive role in improving the local JC. More residual melts and impurity phases were observed in SA than in SB, which had a negative impact on the superconducting properties. Thus, SB exhibited a better trapped field and JC.

A combined powder melt and infiltration growth technique for fabricating nano-composited Y-Ba-Cu-O single-grain superconductor

A new RE + 011 TSIG method for the fabrication of high quality and large size single domain YBCO bulk superconductors

Essential role of liquid phase on melt-processed GdBCO single-grain superconductors

A practical processing method for fabrication of single-domain YBCO superconductors using large-sized GdBCO seed crystals

A reliable technique to fabricate superconducting joints between single grain, Y–Ba–Cu–O bulk superconductors

Enhanced performance of GdBCO bulk superconductors by doping a new kind of YGdBa4CuNbOy nanoparticles

Study On The Technology And Property For Y2bacuo5 Particles Artificial Doping To Obtain Single-Crystal Domain Melt-Textured Ybco Bulk Superconductor

Enhancement of Pinning Role by Nonstoichiometry in YBa2Cu3O7−y Superconductors

Efficient Fabrication of Ultralight YBa 2 Cu 3 O 7− x Superconductors with Programmable Shape and Structure

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

A new seeding technique for the reliable fabrication of large, SmBCO single grains containing silver using top seeded melt growth

A Novel Method to Enhance the Content and size of Y-211 Particles in YBCO bulk Superconductors Grown by RE+011 TSIG Process

Significantly Improving the Flux Pinning of YBa2Cu3O7‐δ Superconducting Coated Conductors via BaHfO3 Nanocrystal Addition Using Multistep Film Growth Method

Optimisation of the processing parameters for the fabrication of high-quality joints between Y-Ba-Cu-O single grain, bulk superconductors

The Performance of the Two-Seeded GdBCO Superconductor Bulk with the Buffer by the Modified TSMG Method

Preparation of YBCO superconducting thick films On MgO substrates by modified melt growth process

Enhanced magnetic properties of YBa2Cu3O7−δ bulk superconductors with tailored structure by a novel seeding assembly

Influence of Ag Doping on Thermal Conductivity and Magnetic Levitation of Single Grain Ybco Superconductors for High-Temperature Superconducting Maglev

Flux Pinning Properties of Single-Grain Bulk GdBCO Superconductors Processed by Different Thicknesses of Y123 Liquid Source

YBCO single grains seeded by 45° - 45° bridge-seeds of different lengths

An in situ self-assembly strategy for exact-(110)-plane-controlled crystallization of high-performance YBa2Cu3O7−δ single grains