Abstract:Two-dimensional transition metal dichalcogenide (TMDC) nanocrystals (NCs) exhibit unique optical and electrocatalytic properties. However, the growth of uniform and high-quality NCs of monolayer TMDC remains a challenge. Until now, most of them are synthesized via a solution-based hydrothermal process or ultrasonic exfoliation method, in which the capping ligands introduced from organic solution often quench the optical and electrocatalytic properties of TMDC NCs. Moreover, it is difficult to homogeneously disperse the solution-based TMDC NCs on a substrate for device fabrication, since the dispersed NCs can easily aggregate. Here, we put forward a novel CVD method to grow closely spaced MoS2 NCs around 5 nm in lateral size. TEM and AFM characterizations demonstrate the monolayer and high-crystalline nature of MoS2 NCs. An obvious blue-shift with 130 meV in photoluminescence signals can be observed. The MoS2 NCs also show an outstanding surface-enhanced Raman scattering for organic molecules due to their localized surface plasmon and abundant edge sites and exhibit excellent electrocatalytic properties for the hydrogen-evolution reaction with a very low onset potential of ∼50 mV and Tafel slope of ∼57 mV/decade. Finally, we further demonstrate this kind of CVD method as a versatile platform for the growth of other TMDC NCs, such as WSe2 and MoSe2 NCs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c14136.Additional AFM and TEM images of MoS2 NCs that were grown over a series of temperatures and time. Raman and EDS mapping of as-grown MoS2 NCs. AFM images of as-grown WSe2 and MoSe2 NCs. SERS performance of RhB molecules dispersed on MoS2 NCs grown on original sapphire and RhB on blank sapphire (PDF)This article has not yet been cited by other publications.

Influence of seeding promoters on the properties of CVD grown monolayer molybdenum disulfide

Effects of inorganic seed promoters on MoS2 few-layers grown via chemical vapor deposition

Dual-Additive Assisted Chemical Vapor Deposition for the Growth of Mn-Doped 2D MoS<sub>2</sub> with Tunable Electronic Properties

Detrimental Influence Of Catalyst Seeding On The Device Properties Of Cvd-Grown 2d Layered Materials: A Case Study On Mose2

Substrate Lattice-Guided Seed Formation Controls the Orientation of 2D Transition-Metal Dichalcogenides

The Photoresponsivity of Monolayer Molybdenum Disulfide Grown by Chemical Vapor Deposition with Different Seeding Promoters

Experimental and theoretical investigation on pre-deposited precursor as growth sites for monolayer MoS 2 growth by supercritical fluid deposition

Perforated Carbon Nanotube Film Assisted Growth of Uniform Monolayer MoS2.

Growth of High-Quality Monolayer Transition Metal Dichalcogenide Nanocrystals by Chemical Vapor Deposition and Their Photoluminescence and Electrocatalytic Properties

Promotion of Mo-based Ionic Crystal Precursor for MoS2 Wafer Growth

Pattern Stimulated CVD Growth of 2D MoS2

Effect of different precursors on CVD growth of molybdenum disulfide

Spontaneous n-Doping in Growing Monolayer MoS 2 by Alkali Metal Compound-Promoted CVD

Catalytic strategies for uniform monolayer MoSe 2 growth in CVD processes

Liquid-phase catalyst pre-seeding for controlled growth of layered MoS2 films over a large area via chemical vapor deposition

Application-Oriented Growth of a Molybdenum Disulfide (MoS2) Single Layer by Means of Parametrically Optimized Chemical Vapor Deposition

Substrate effects on the CVD growth of MoS2 and WS2

Boosting Monolayer Transition Metal Dichalcogenides Growth by Hydrogen-Free Ramping during Chemical Vapor Deposition

Controllable Growth of Monolayer MoS2by Chemical Vapor Deposition Via Close MoO2precursor for Electrical and Optical Applications

Influence of substrate placement on synthesis of two-dimensional MoS2

Capture the growth kinetics of CVD growth of two-dimensional MoS2