Abstract:The widespread use of sodium aluminosilicate glass in many engineering applications due to its mechanical and optical properties (transparency, dielectric, etc.), has become common in recent years. However, glass, a brittle material, has its vulnerability to fracture. Processes such as heat treatment (heat tempering) or chemical strengthening through ion-exchange have been used to create residual stress profiles on the glass, in a bid to improve its fracture strength. However, failure still occurs, which is mostly catastrophic and expensive to repair. Therefore understanding, predicting, and eventually improving the resistance to damage or fracture of chemically strengthened glass is important to designing new glasses that would be tougher while retaining their transparency. The relationship between the glass residual stress parameters such as the compressive stress (CS), depth of compression layer (DOL), and central tension (CT) versus apparent (effective) fracture toughness for different crack depth was investigated in this study using a Silicon Carbide particle blast plus ring-on-ring (RoR) test method. The results also showed that improving the fracture resistance of glass via chemical strengthening requires a proper combination of CS, DOL, and CT, which is particularly dependent on the initial/existing crack (flaw) depth. It was determined that for a damage event involving the introduction of a shallow crack depth, the criterion for optimal resistance to fracture, in terms of apparent fracture toughness, is weighted more towards a high CS, than deep DOL while for a deep flaw damage event, it is more weighted towards deep DOL, than a high CS. These results provide a valuable piece of information in the design of a more robust glass in engineering applications.

Accelerated life test of chemically strengthened light weight glass bottles by spray coating

Weibull Reliability and Mechanical Properties of Chemical Strengthened Lightweight Glass Containers Using Spray Coating

Chemical strengthening of high aluminosilicate glasses and experimental fitting

Influence of Zirconia Sol-Gel Coating on Fracture Strength of Chemical Strengthened Soda Lime Glass

Chemical strengthening of glass powder particles

Influence of AC-DC-AC Cycling with Hydrostatic Pressure on Accelerated Protective Performance Test of Glass Flake Epoxy Coating

Accelerated Zero-Stress Hydrothermal Aging of Dry E-Glass Fibers and Service Life Prediction Using Arrhenius Model

Surface treatments on commercial glasses: durable impact on the retention of lead, barium and boron

Enhancement of Durability of Glass Fiber-Reinforced Cement with PVA

A durable coating to prevent stress corrosion effects on the surface strength of annealed glass

Enhancing the design bending strength of new and aged glass with a functional coating

Effect of Early Water Exposure on the Strength of Glass Ionomer Restoratives

A New Method for Evaluating the Influence of Coatings on the Strength and Fatigue Behavior of Flexible Glass

The Competing Effect of Initial Crack Depth Versus Chemical Strengthening Parameters on Apparent Fracture Toughness of Sodium Aluminosilicate Glass

Combined Effects of Sustained Loads and Wet-Dry Cycles on Durability of Glass Fiber Reinforced Polymer Composites

Steam strengthened glass

Influence of accelerated aging on mechanical properties and aging behavior of glass fiber reinforced pipe

Enhancing bending performance of ultrathin flexible glass through chemical strengthening

Glass flakes for enhancing mechanical properties of glass/epoxy composites

Hardness and scratch resistance of chemically strengthened alkali‐borosilicate thin glass

Surface damage resistance and yielding of chemically strengthened silicate glasses: From normal indentation to scratch loading