Abstract:Polyimide (PI) films have excellent comprehensive properties and bright prospects in the next generation of optoelectronic and microelectronic applications. PIs were synthesized by aromatic diamines and alicyclic dianhydrides considered to be the most effective method for preparing polyimides with high light transmittance and low dielectric constant. In order to improve the overall performance of polyimide, the introduction of a large trifluoromethyl group into the main chain is also considered a powerful strategy. In this article a novel diamine containing 6 trifluoromethyl groups has been designed and synthesized by Suzuki reaction. Afterwards, PIs were synthesized with fluorinated aromatic dianhydride and alicyclic dianhydride through a two-step method. The two PIs have excellent solubility: PI-a and PI-b exhibited excellent solubility in common polar solvents. Such as DMF, DMAc, NMP and DMSO at room temperature, and PI-a was soluble in low-boiling solvents such as ethyl acetate, CH2Cl2 and CHCl3 at room temperature. PI-b was soluble in low-boiling solvents acetone and CHCl3 at room temperature, which was rarely seen in other aromatic polyimides. Soluble in common organic solvents, especially low boiling point solvents, made these polymers easy to process and suitable for processing technology in solution. This was an important modification for PIs. They also showed good high temperature resistance: the decomposition temperature (T5%) of two PIs were 520 °C and 475 °C. In addition, the residual rate at 790 °C was 50 % and 49 % respectively. Two PI films had a very low dielectric constant 2.26 and 2.24, respectively, which was attributed to the hyperbranched structure and strong electron-withdrawing fluorine-containing groups. PI-a and PI-b also had low water absorption of 0.66 % and 0.72 %, respectively. The transmittance of PI-a and PI-b high transparent films at 450 nm were 74% and 82%, respectively. The significant optical modification was mainly due to the weak electron-accepting alicyclic unit and the large trifluoromethyl electron withdrawing group. This work mainly provided an effective strategy for synthesizing comprehensive excellent performance PIs with high transmittance, excellent solubility, low water absorption, high heat resistance and low dielectric constant.

Colorless and transparent semi‐alicyclic polyimide films with intrinsic flame retardancy based on alicyclic dianhydrides and aromatic phosphorous‐containing diamine: Preparation and properties

Preparation and properties of light-colored and transparent semi-alicyclic polyimide films with enhanced flame retardancy from alicyclic dianhydrides and aromatic diamine containing phenolphthalein unit

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

A phosphorus-, nitrogen- and carbon-containing polyelectrolyte complex: preparation, characterization and its flame retardant performance on polypropylene

Synthesis and Characterization of Semi-Alicyclic Transparent Polyimide Films Containing Benzanilide and Fluorene Units with Improved High-Temperature Dimensional Stability and Low-Optical Retardations

Synthesis and properties of polyimides from a diamine containing side diphenylphosphine oxide and trifluoromethyl groups

Heat‐resistant and transparent polyimides derived from alicyclic dianhydrides and phthalazinone‐based diamine

Synthesis and Characterization of Organo-Soluble Polyimides Based on Polycondensation Chemistry of Fluorene-Containing Dianhydride and Amide-Bridged Diamines with Good Optical Transparency and Glass Transition Temperatures over 400 °C

Preparation and properties of semi-alicyclic thermoplastic polyimide sheets from stereoisomeric hydrogenated pyromellitic dianhydrides and fluorinated diamine

Design, Synthesis and Properties of Semi-Alicyclic Colorless and Transparent Polyimide Films with High Glass Transition Temperatures and Low Retardation for Potential Applications in Flexible Electronics

Preparation and Properties of Pale‐colored and Optically Transparent Fluoro‐containing Polyimide Films with Low Solar Absorptivity and Enhanced High‐temperature Dimensional Stability for Potential Applications in Space Environments

Preparation and Characterization of Atomic Oxygen-Resistant, Optically Transparent and Dimensionally Stable Copolyimide Films from Fluorinated Monomers and POSS-Substituted Diamine

Synthesis and Properties of Optically Transparent Fluoro-Containing Polyimide Films with Reduced Linear Coefficients of Thermal Expansion from Organo-Soluble Resins Derived from Aromatic Diamine with Benzanilide Units

Synthesis and properties of novel colorless and thermostable polyimides containing cross‐linkable bulky tetrafluorostyrol pendant group and organosoluble triphenylmethane backbone structure

High Optical Transparency, Low Dielectric Constant and Light Color of Organosoluble Fluorinated Polyimides Based on 10,10-Bis[4-(4-amino-3-trifluoromethylphenoxy)phenyl]-9(10h)-anthrone

Preparation and properties of colorless and transparent semi‐alicyclic polyimide films with enhanced high‐temperature dimensional stability via incorporation of alkyl‐substituted benzanilide units

Colorless Poly(amide-imide)s with Low Dielectric Constants and Enhanced Mechanical Properties through Tri-Armed Cross-Linkers

Preparation and characterization of organic soluble polyimides with low dielectric constant containing trifluoromethyl for optoelectronic application

Preparation and Characterization of Light-Colored Polyimide Nanocomposite Films Derived from a Fluoro-Containing Semi-Alicyclic Polyimide Matrix and Colloidal Silica with Enhanced High-Temperature Dimensionally Stability

Synthesis and thermal behavior of a novel UV-curable transparent flame retardant film and phosphorus-nitrogen synergism of flame retardancy