Abstract:A voltammetric approach was developed for the selective and sensitive determination of hydrogen peroxide using Au plated porous silicon (PSi) nanopowder modified glassy carbon electrode (GCE). The AuNPs-PSi hybrid structure was synthesized via stain etching procedure followed by an immersion plating method to deposit AuNPs onto PSi via a simple galvanic displacement reaction with no external reducing agent to convert Au3+ to Au0. The as-fabricated AuNPs-PSi catalyst was successfully characterized by XRD, Raman, FTIR, XPS, SEM, TEM and EDS techniques. Well crystalline nature of the as-fabricated hybrid structure with AuNPs size ranging from 5 to 40 nm was observed. The specific surface area and total pore volume for both PSi and AuNPs plated PSi were evaluated using N2 adsorption isotherm technique. Cyclic voltammetry and electrochemical impedance spectroscopy techniques were applied to investigate the catalytic efficiency of AuNPs-PSi modified electrode compared to pure PSi/GCE and unmodified GCE. The sensing performance of the active material modified GCE was thoroughly examined with linear sweep voltammetry (LSV) and square wave voltammetry (SWV) techniques. The AuNPs-PSi/GCE exhibited a remarkable linear dynamic range between 2.0 and 13.81 mM (for LSV) and 0.5-6.91 mM for (SWV) with high sensitivity and low detection limit of 10.65 μAmM-1cm-2 and 14.84 μM for LSV, whereas 10.41 μAmM-1cm-2 and 15.16 μM using SWV techniques, respectively. The fabricated sensor electrode showed excellent anti-interfering ability in the presence of several common biomolecules as well as demonstrated good operational stability and reproducibility with low relative standard deviation. Moreover, the modified electrode showed acceptable recovery of H2O2 in a real sample analysis. Thus, the developed AuNPs-PSi hybrid nanomaterial represents an excellent electrocatalyst for the efficient detection and quantification of H2O2 by the electrochemical approach.

Prussian Blue Modified Submicron Structured Gold Electrodes for Amperometric Hydrogen Peroxide Sensing

Electrodeposition of Monodispersed Cu Nanoparticles on Poly-P-Aminobenzene Sulfonic Acid Functionalized Glassy Carbon Electrode and the Electrocatalytic Reduction Toward H2o2

A Hydrogen Peroxide Sensor Prepared By Electropolymerization Of Pyrrole Based On Screen-Printed Carbon Paste Electrodes

The influence of deposition time on electrochemical performance of Prussian blue-modified submicron-structured gold electrodes for hydrogen peroxide sensing

Plasmonic Imaging Of Electrochemical Reactions At Individual Prussian Blue Nanoparticles

Hydrogen Peroxide Sensor Based on Electrodeposited Prussian Blue Film

Prussian blue@Au nanoparticles/SiO2 cavity/ITO electrodes: Application as hydrogen peroxide sensor

Optimized deposition time boosts the performance of Prussian blue modified nanoporous gold electrodes for hydrogen peroxide monitoring

Synergetic effect of Prussian blue film with gold nanoparticle graphite–wax composite electrode for the enzyme-free ultrasensitive hydrogen peroxide sensor

High-Linearity Hydrogen Peroxide Sensor Based on Nanoporous Gold Electrode

Synthesis, Characterization, and Immobilization of Prussian Blue-Modified Au Nanoparticles: Application to Electrocatalytic Reduction of H2O2

Fabrication of gold microelectrodes on polystyrene sheets by UV-directed electroless plating and its application in electrochemical detection

Synthesis, characterization, and electrochemical sensor application of Prussian blue nanocubes/Au nanocomposite for hydrogen peroxide sensing

Direct Electrodeposition of Bimetallic Nanostructures on Co-Based MOFs for Electrochemical Sensing of Hydrogen Peroxide

Hydrogen peroxide biosensor based on direct electrochemistry of hemoglobin immobilized on gold nanoparticles in a hierarchically porous zeolite

Ag Functionalized Molybdenum Disulfide Hybrid Nanostructures for Selective and Sensitive Amperometric Hydrogen Peroxide Detection

Hydrogen peroxide sensor based on horseradish peroxidase-labeled Au colloids immobilized on gold electrode surface by cysteamine monolayer

Prussian blue hollow nanostructures: Sacrificial template synthesis and application in hydrogen peroxide sensing

Non-enzymatic Hydrogen Peroxide Detection Using Gold Nanoclusters-Modified Phosphorus Incorporated Tetrahedral Amorphous Carbon Electrodes

Gold nanoparticles plated porous silicon nanopowder for nonenzymatic voltammetric detection of hydrogen peroxide

Nonenzymatic Hydrogen Peroxide Electrochemical Sensor Based on Au-Hs/So3h-Pmo (et) Nanocomposite