Abstract:A modified ZSM-5 zeolite (denoted as ZSM-5-M), which was synthesized using tetrapropylammonium hydroxide (TPAOH) and cetyltrimethylammonium bromide (CTAB) as dual templates, and the commercial ZSM-5 zeolite (denoted as ZSM-5-C), have been used to prepare the corresponding CuZSM-5 (M & C) catalysts containing 3 wt% Cu by ion exchange method. Compared to CuZSM-5-C catalyst, the CuZSM-5-M catalyst demonstrated remarkably higher catalytic activity at low temperatures (<450 °C) for selective catalytic reduction of NOx with NH3 both in the simulated exhaust and engine bench testing. The modified synthesis by the dual template with the product aged for a long time at room temperature, leads to the formation of the ZSM-5-M zeolite with much higher specific surface area (608 m2 g−1) and higher total pore volume (0.8880 cm3 g−1) due to the presence of more mesoporous pores. The X-ray diffraction results showed that ZSM-5-M maintained its typical MFI structure, while its crystallinity (84.1%) was lower than that of the ZSM-5-C zeolite. The characterization results by H2 temperature-programmed reduction and X-ray photoelectron spectra revealed that the higher redox properties of isolated Cu2+ ions combined with the high-dispersion CuO crystallites and Cu+ ions are likely the main cause for the excellent low-temperature activity of the CuZSM-5-M catalysts. The isolated active Cu2+ species and high-dispersion CuO crystallites had a stronger interaction with other atoms in CuZSM-5-M catalysts. The results from thermogravimetric analysis, temperature-programmed desorption of ammonia and in situ diffuse reflectance infrared Fourier transform spectroscopy demonstrated that ZSM-5-M is a strong Bronsted acid site and the CuZSM-5-M catalyst had a relatively higher exchange rate of Cu2+ and Cu+ ions and more Lewis acidic sites, giving it a high NH3 adsorption capacity. The strong Bronsted acid site might be another cause that results in the higher NH3-SCR performance of the CuZSM-5-M catalyst.

Effect of copper precursors on the catalytic performance of Cu-ZSM-5 catalysts in N2O decomposition

Catalytic Decomposition of N2o over Cu-Zsm-5 Nanosheets

Catalytic Decomposition of N2O over Cu-ZSM-11 Catalysts

The Oscillatory Behaviour of Cu‐ZSM‐5 Catalysts for N2O Decomposition: Investigation of Cu species by complementary techniques

CoZSM-11 Catalysts for N2O Decomposition: Effect of Preparation Methods and Nature of Active Sites

Effect of the Crystal Size of Cu-ZSM-5 on the Catalytic Performance in N2O Decomposition

A novel Cu-Mo/ZSM-5 catalyst for NOx catalytic reduction with ammonia

Effect of Cu-ZSM-5 catalysts with different CuO particle size on selective catalytic oxidation of N,N-Dimethylformamide

Synthesis and evaluation of mesopore structured ZSM-5 and a CuZSM-5 catalyst for NH3-SCR reaction: Studies of simulated exhaust and engine bench testing

Preparation and Characterization of Mesoporous CuO/ZSM-5 Catalysts for Automotive Exhaust Purification

Catalytic Decomposition of N2O over Fe-ZSM-11 Catalysts Prepared by Different Methods: Nature of Active Fe Species

Promoting effect of Cu and Mn doping on the Fe/ZSM-5 catalyst for selective catalytic reduction of NO with NH 3

Silicalite-1@Cu-ZSM-5 core-shell catalyst for N2O decomposition

Effects of Different Copper Species on the Combustion of Dichloromethane over Cu/HZSM-5 Zeolite Nanoporous Catalysts

Effect of the preparation method on activity of Cu-ZSM-5 nanocatalyst for the selective reduction of NO by NH3

Structural Evolution and Catalytic Properties of Nanostructured Cu/Zro2 Catalysts Prepared by Oxalate Gel-Coprecipitation Technique

Hybrid Cu-Fe/ZSM-5 Catalyst Prepared by Liquid Ion-Exchange for NOx Removal by NH3-SCR Process

Insights into the Precursor Effect on the Surface Structure of Γ-Al2o3 and NO + CO Catalytic Performance of CO-pretreated CuO/MnOx/γ-Al2O3 Catalysts.

Improving Catalytic Performance and Stability of Copper-Zinc Based Catalyst on Aluminum Nitride for Formaldehyde Removal from Crude Trioxane

Effect of addition of Zn on the catalytic activity of a Co/HZSM-5 catalyst for the SCR of NOx with CH4

Effect of Preparation Method on Cu Active Sites and the Reaction Pathway in NO Reduction by NH 3 over Cu–SSZ-13