Abstract:High strength low alloy (HSLA) steels are widely used in the construction of ship structures, oil pipelines, offshore platforms and so on because of their good strength, toughness and weldability. HSLA steel is generally designed with low carbon and Cu alloying. Tempered lath bainite or martensite and nano-precipitate phase of Cu can be obtained by quenching and ageing process after rolling to ensure the excellent matching of strength, low temperature toughness and weldability of HSLA steel. At present, increasing attention has been focused on the precipitation behavior and strengthening mechanism of Cu particles in HSLA steel which was aged at the peak hardness of ageing curve. However, in practical engineering applications, overageing heat treatment is generally used to make HSLA steel achieve a good match of strength and toughness. In this work, the microstructure and nano-sized Cu precipitates of an industrial production HSLA steel plate with thickness of 35 mm were characterized by SEM, EBSD, HRTEM and APT. Meanwhile, the strengthening mechanism of the tested steel was investigated. The results show that Cu precipitates in the tested steel processed by overageing are mainly in the range of 6 similar to 50 nm, Cu particles exhibiting short rod or spherical shape within 30 nm are 9R structure, and other particles size larger than 30 nm exhibiting long rod or spherical shape are fcc structure. The segregation of trace Mn and Ni in rod particles on the interface between Cu particles and matrix is more obvious. After ageing at a higher temperature range, the yield strength of the tested steel decreases linearly with the increase of tempering temperature. The main strengthening mechanism of the HSLA steel is fine grain strengthening, followed by dislocation strengthening and precipitation strengthening. The calculated results show that every 1% Cu added in the tested steel can produce about 90 MPa precipitation strengthening increment under the condition of overageing heat treatment. The strength difference between the surface and the center of the tested steel plate is about 40 MPa, which is mainly due to the difference of grain size and dislocation density of steel.

Hierarchical Cu Precipitation in Lamellated Steel after Multistage Heat Treatment

Regulation of Cu Precipitation by Intercritical Tempering in A Hsla Steel

High-resolution Transmission Electron Microscopy Characterization of the Structure of Cu Precipitate in a Thermal-aged Multicomponent Steel

Effect of Multistage Heat Treatment on Microstructure and Mechanical Properties of High-Strength Low-Alloy Steel

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Investigation of Hierarchical Precipitation on Bimodal-Grained Austenite and Mechanical Properties in Quenching-Partitioning-tempering Steel

Investigation of the Crystallographic Evolution Sequence of Nano-Precipitation via HRTEM in Cu-Bearing Ultra-Low Carbon Steel

Strengthening of Ni-Mn-Cu-Al-Co steel by nanoscale Cu and β-NiAl co-precipitated couples

Compositional Variants of Cu-rich Precipitate in Thermally Aged Ferritic Steel

Analyzing the Precipitation Effects in Low-Alloyed Copper Alloys Containing Hafnium and Chromium

Reinforced Cu Precipitation Strengthening by Matrix Transformation from Martensite to Austenite in High-Strength Low-Alloy Steel

Characterization of Nano-Sized Precipitation and Dislocations and the Correlation with Mechanical Properties of a Low Alloy TRIP-aided Steel

Study on Diversified Carbide Precipitation in High‐Strength Low‐Alloy Steel during Tempering

Nano-sized Austenite and Cu Precipitates Formed by Using Intercritical Tempering Plus Tempering and Their Effect on the Mechanical Property in a Low Carbon Cu Bearing 7 Ni Steel

Characterization of Precipitates in X12CrMoWVNbN10-1-1 Steel During Heat Treatment

Correlation of Cu precipitation with austenite–ferrite transformation in a continuously cooled multicomponent steel: An atom probe tomography study

Precipitation behavior and microstructural evolution during thermo-mechanical processing of precipitation hardened Cu-Hf based alloys

Compositional and structural characterization of alloyed carbide by 3D atom probe and high-resolution TEM

Concurrent Recrystallization and Precipitation for Combination of Superior Precipitation and Grain Boundary Hardening in Co37Cr20Ni37Ti3Al3 High-Entropy Alloy

Mechanical Properties and Nanoparticles Precipitation Behavior of Multi-Component Ultra High Strength Steel

The Strengthening Mechanism of Cu Bearing High Strength Steel As-Quenched and Tempered and Cu Precipitation Behavior in Steel