Enhanced dielectric tunability and reduced dielectric loss in the La/Fe co-doped Ba0.65Sr0.35TiO3 ceramics
Wenfeng Liu,Yi Zhao,Yihang Jin,Fanyi Kong,Jinghan Gao,Shengtao Li
DOI: https://doi.org/10.1016/j.jallcom.2022.163642
IF: 6.2
2022-04-01
Journal of Alloys and Compounds
Abstract:In the present study, (Ba0.65Sr0.35)1−xLaxTi1−xFexO3(x = 0, 0.0025, 0.005, 0.01) ceramics were designed and prepared by the conventional solid-state reaction method. The microstructures and electrical properties of La/Fe co-doped Ba0.65Sr0.35TiO3 ceramics were investigated. Enhanced dielectric tunability and reduced dielectric loss were achieved in this system. The acceptor dopant Fe3+ was used to lower dielectric loss while the donor dopant La3+ was added to improve dielectric tunability. The optimum tunable properties took place at x = 0.0025 with the dielectric tunability = 78.8% and the dielectric loss = 0.0040. The figure of merit (FOM) was improved to 197, about five times that of pure BST. The breakdown strength (BDS) enhanced from 59.9 kV/cm to 111.4 kV/cm by La3+ and Fe3+ dopant, which promoted the stability of BST ceramics under high applied electric field. In conclusion, excellent tunable properties and improved breakdown strength made it possible for the La/Fe co-doped BST ceramics to be promising for tunable microwave applications.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering