Structure–dielectric properties relationship in Mg–Mn co-doped Ba<sub>0.4</sub>Sr<sub>0.6</sub>TiO<sub>3</sub>/MgAl<sub>2</sub>O<sub>4</sub>tunable microwave composite ceramics
Jingji Zhang,Jiwei Zhai,Mingwei Zhang,Peng Qi,Xian Yu,Xi Yao
DOI: https://doi.org/10.1088/0022-3727/42/7/075414
2009-01-01
Abstract:xMgO-yMnCO(3)-0.70(1 - x - y)Ba0.4Sr0.6TiO3-0.30(1 - x - y)MgAl2O4 (where x, y = 0.0 wt% and x = 1.0 wt%, y = 0.5, 1.0, 2.0, 5.0, 10.0 wt%) composite ceramics synthesized by the solid-state reaction show two crystalline phases, corresponding to the Ba0.4Sr0.6TiO3 and MgAl2O4 phases. At a low MnCO3 content (y <= 2.0 wt%), weak diffuseness is visible, while strong diffuseness is observed for a higher MnCO3 content. For x = 0.01 and 0.01 <= y <= 0.02, high tunability is attributed to the small cooperative displacements of Ti4+ ions in the close packed oxygen octahedra of the BST system. The Q value gradually increases with y, potentially due to the microstructural evolution of the BST lattice structure characterized by Raman spectra. Interestingly, the high Q value of the composition with x = 0.01 and y >= 0.05 is in a wide frequency range, which may play an important role in the engineering of the electric-field tunable microwave elements.