Nanoscale Morphologies on the Surface of 3D-Printed Titanium Implants for Improved Osseointegration: A Systematic Review of the Literature
Shiyan Yang,Weibo Jiang,Xiao Ma,Zuobin Wang,Robert L Sah,Jincheng Wang,Yang Sun
DOI: https://doi.org/10.2147/ijn.s409033
IF: 7.033
2023-07-27
International Journal of Nanomedicine
Abstract:Shiyan Yang, 1, &ast Weibo Jiang, 1, &ast Xiao Ma, 2, &ast Zuobin Wang, 3 Robert L Sah, 4, 5 Jincheng Wang, 1 Yang Sun 1 1 Orthopedic Medical Center, the Second Hospital of Jilin University, Changchun, Jilin, 130000, People's Republic of China; 2 Department of Orthopedics, the China-Japan Union Hospital of Jilin University, Changchun, Jilin, 130000, People's Republic of China; 3 International Research Centre for Nano Handling and Manufacturing of China, Changchun University of Science and Technology, Changchun, Jilin, 130000, People's Republic of China; 4 Department of Bioengineering, University of California–San Diego, La Jolla, CA, 92037, USA; 5 Center for Musculoskeletal Research, Institute of Engineering in Medicine, University of California–San Diego, La Jolla, CA, 92037, USA &astThese authors contributed equally to this work Correspondence: Yang Sun, Orthopedic Medical Center, the Second Hospital of Jilin University, Changchun, 130000, Jilin, People's Republic of China, Tel/Fax +86 18744000871, Email Three-dimensional (3D) printing is serving as the most promising approach to fabricate personalized titanium (Ti) implants for the precise treatment of complex bone defects. However, the bio-inert nature of Ti material limits its capability for rapid osseointegration and thus influences the implant lifetime in vivo. Despite the macroscale porosity for promoting osseointegration, 3D-printed Ti implant surface morphologies at the nanoscale have gained considerable attention for their potential to improve specific outcomes. To evaluate the influence of nanoscale surface morphologies on osseointegration outcomes of 3D-printed Ti implants and discuss the available strategies, we systematically searched evidence according to the PRISMA on PubMed, Embase, Web of Science, and Cochrane (until June 2022). The inclusion criteria were in vivo (animal) studies reporting the osseointegration outcomes of nanoscale morphologies on the surface of 3D-printed Ti implants. The risk of bias (RoB) was assessed using the Systematic Review Centre for Laboratory Animal Experimentation (SYRCLE's) tool. The quality of the studies was evaluated using the Animal Research: Reporting of In Vivo Experiments (ARRIVE) guidelines. (PROSPERO: CRD42022334222). Out of 119 retrieved articles, 9 studies met the inclusion criteria. The evidence suggests that irregular nano-texture, nanodots and nanotubes with a diameter of 40– 105nm on the surface of porous/solid 3D-printed Ti implants result in better osseointegration and vertical bone ingrowth compared to the untreated/polished ones by significantly promoting cell adhesion, matrix mineralization, and osteogenic differentiation through increasing integrin expression. The RoB was low in 41.1% of items, unclear in 53.3%, and high in 5.6%. The quality of the studies achieved a mean score of 17.67. Our study demonstrates that nanostructures with specific controlled properties on the surface of 3D-printed Ti implants improve their osseointegration. However, given the small number of studies, the variability in experimental designs, and lack of reporting across studies, the results should be interpreted with caution. Keywords: nano-pattern, 3D-printed, titanium implant, surface modification, osseointegration In the past decade, additive manufacturing, also known as three-dimensional (3D) printing, has become a promising technology for the production of orthopedic implants due to its ability to produce customized shapes for the precise treatment of complex bone defects, which are difficult to conquer with traditional methods. 1–4 Based on the computer-aided manufacturing, laser technology, numerical control technology, and polymer materials, 3D printing has shown remarkable advantages, including single-piece customization, adjustment of mechanical strength, and high process efficiency. 5 Selective laser melting (SLM), selective laser sintering (SLS), electron beam melting (EBM), laser engineered net shaping (LENS), and direct metal laser sintering (DMLS) are the main technologies for manufacturing 3D-printed orthopedic implants, with commercially pure titanium (cp Ti) and Ti alloys (mainly Ti6Al4V) serving as the most common materials being used due to their biocompatibility, low toxicity, high corrosion resistance, high-strength-to-weight ratio, resistance to fatigue deformation and excellent mechanical properties. 6–8 However, as a bio-inert material, surface-unmodified Ti lacks biointegration capability and has a far higher elastic modulus (110–120 GPa) than that of cortical bone (10–30 GPa), which limits the long-term fixation and lifespan of Ti implants. 9 Homogeneou -Abstract Truncated-
pharmacology & pharmacy,nanoscience & nanotechnology