Abstract:Abstract Large surface area, high conductivity, and rich active site of carbon electrode materials are necessary characteristics for energy storage devices. However, high conductivity and high nitrogen doping of carbon electrode materials are difficult to coordinate. Here, a facile method via the carbonization of nitrogen‐containing Schiff base polymer has been developed to prepare high conductivity and high nitrogen‐doped hierarchical porous carbon. The organic components with a benzene ring structure in the polymer promote the formation of more sp2‐graphitized carbon, which is beneficial for the improvement of electrical conductivity. Nitrogen‐doped hierarchical porous carbon calcined at 900°C under the NH3 atmosphere possesses high nitrogen content of 7.48 at%, a large specific surface area of 1613.2 m2/g, and high electrical conductivity of 2.7 S/cm. As electrode materials in an aqueous‐based supercapacitor, nitrogen‐doped hierarchical porous carbon exhibits superior specific capacitance of 385 F/g at 1 A/g as well as excellent rate performance (242 and 215 F/g at a current density of 100 and 200 A/g, respectively). In addition, the specific capacitance of electrode measured in a two‐electrode system is 335 F/g at 1 A/g, and the long‐term cycling stability can be achieved with more than 94% initial capacitance after 10 000 cycles. The constructed symmetric supercapacitor delivers high energy density and high power density. The outstanding electrochemical performances combined with the novel and scalable synthetic approach make the nitrogen‐doped hierarchical porous carbon potential electrode material for electrochemical devices.

Nitrogen Doped Macroporous Carbon As Electrode Materials For High Capacity Of Supercapacitor

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Micro-Spatial Hydrothermal Preparation of Nitrogen-doped Carbon/NiCo2S4 Electrode Material for Supercapacitors

Synthesis of Nitrogen-Doped Porous Carbon Nanofibers As an Efficient Electrode Material for Supercapacitors.

Facile synthesis of microporous N-doped carbon material and its application in supercapacitor

A Nitrogen-doped Hierarchical Mesoporous/Microporous Carbon for Supercapacitors

N-doped Hierarchically Micro- and Mesoporous Carbons with Superior Performance in Supercapacitors

Facile synthesis of nitrogen-enriched nanoporous carbon materials for high performance supercapacitors.

Nitrogen and Sulfur Codoped Porous Carbon Microsphere: a High Performance Electrode in Supercapacitor

Nitrogen-Doped Mesoporous Carbon Microspheres by Spray Drying-Vapor Deposition for High-Performance Supercapacitor

Synthesis of n-doped mesoporous carbon by silica assistance as electrode for supercapacitor

Nitrogen-doped hierarchical porous carbon as an efficient electrode material for supercapacitors

Facile synthesis of porous carbon materials with extra high nitrogen content for supercapacitor electrodes

Nitrogen-doped macro-meso-micro hierarchical ordered porous carbon derived from ZIF-8 for boosting supercapacitor performance

Nitrogen‐doped Hierarchical Few‐layered Porous Carbon for Efficient Electrochemical Energy Storage

Nitrogen/Phosphorus Co-Doped Porous Carbon Materials For Supercapacitor Electrodes

Nitrogen-doped micro-nano carbon spheres with multi-scale pore structure obtained from interpenetrating polymer networks for electrochemical capacitors

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors

A Nitrogen-Doped Ordered Mesoporous Carbon Nanofiber Array For Supercapacitors

Nitrogen-doped Hierarchically Ellipsoidal Porous Carbon Derived from Al-based Metal-Organic Framework with Enhanced Specific Capacitance and Rate Capability for High Performance Supercapacitors

Nitrogen-Doped Hierarchical Porous Carbon Nanowhisker Ensembles on Carbon Nanofiber for High-Performance Supercapacitors